金属薄膜屈服强度的鼓包法表征

发布时间：2018-05-16 17:30

  本文选题：鼓包法 + 镍薄膜　； 参考：《材料科学与工程学报》2017年04期

【摘要】：本文采用鼓包法研究金属薄膜的屈服强度,对具有圆形自由窗口的镍薄膜一侧施加压力,薄膜受压变形的全场形貌用数字散斑相关法(DSCM)进行测量,并应用板壳理论分析小挠度变形下膜内应力分布情况。结果表明:圆形薄膜受压时首先从边缘开始屈服,从压力-挠度曲线偏离线性关系的临界点得到金属镍膜的屈服强度为467MPa,这和单轴拉伸法测量所得到的屈服强度值吻合较好。
[Abstract]:In this paper, the yield strength of metallic thin films is studied by bulging method. The pressure on one side of nickel film with circular free window is applied. The full field morphology of the film under compression deformation is measured by digital speckle correlation method (DSCM). The stress distribution in the film under small deflection deformation is analyzed by using the theory of plate and shell. The results show that the circular film begins to yield from the edge of the film under compression, and the yield strength of the nickel film is 467 MPA from the critical point of the pressure deflection curve deviating from the linear relationship, which is in good agreement with the yield strength measured by uniaxial tensile method.
【作者单位】： 湘潭大学材料科学与工程学院特种功能薄膜材料国家地方联合工程实验室;
【基金】：国家自然科学基金资助项目(11172258) 湖南省科技厅资助项目(2014TT2037) 湘潭大学科研资助项目(13QDZ07,SG2013006)
【分类号】：TB383.2;TG146.15

【相似文献】

相关期刊论文 前7条

1 王立;;硅基铜膜屈服强度的实验研究[J];咸阳师范学院学报;2005年06期

2 熊山江,张涛,王晓薇;铍的微屈服强度测试研究[J];宇航材料工艺;1992年01期

3 景山,李洪钟;负压差散体颗粒无约束屈服强度实验测量方法[J];化工冶金;1997年03期

4 宋名实,姜述春,吴立新,朱清仁;高分子材料的极限断裂强度和破坏性能的研究——Ⅳ.等速拉伸下屈服强度动力学模型理论[J];材料科学进展;1991年04期

5 李莹;;管材弧形试样屈服强度测试的影响因素及原因分析[J];航天制造技术;2012年01期

6 江中浩,连建设,董尚利,扬德庄;短纤维增强金属基复合材料弹性模量和屈服强度不对称性的解释[J];复合材料学报;2000年01期

7 江中浩,连建设,董尚利,扬德庄;短纤维增强金属基复合材料的弹性模量和屈服强度[J];复合材料学报;1999年04期

相关博士学位论文 前1条

1 王玺;SiC/Al复合材料微屈服行为与强化机理研究[D];哈尔滨工业大学;2015年

，

本文编号：1897770