化学镀时间对无纺布表面镍镀层结构影响规律研究
发布时间：2018-07-20 09:18
【摘要】：采用Pd2+活化结合化学镀镍工艺制备金属化的植物纤维无纺布,借助X射线衍射、扫描电镜、四探针等分析测试手段,研究化学镀时间对植物纤维无纺布表面镀镍层结构特性的影响规律。结果表明延长化学镀时间,植物纤维无纺布表面化学镀镍层结晶性能变好。当化学镀时间为10min时,植物纤维无纺布的质量为0.038g/cm2,镀层表面电阻率为0.2Ω·cm。
[Abstract]:The metallized plant fiber non-woven fabric was prepared by PD _ 2 activation combined with electroless nickel plating. By means of X-ray diffraction, scanning electron microscope, four-probe, etc. The effect of electroless plating time on the structure characteristics of nickel coating on the surface of vegetable fiber non-woven fabric was studied. The results show that the crystallization properties of electroless nickel coating on the surface of vegetable fiber nonwoven fabric are improved by prolonging the electroless plating time. When the electroless plating time is 10min, the quality of vegetable fiber nonwoven fabric is 0.038 g / cm ~ 2, and the surface resistivity of the coating is 0.2 惟 cm ~ (2).
【作者单位】： 合肥乐凯科技产业有限公司;合肥学院化学与材料工程系;贺州学院化学与生物工程学院;太原理工大学表面工程研究所;
【基金】：中国科学院能量转换材料重点实验室开放课题基金(KF2016001) 安徽省教育厅一般项目(KJ2015B1105905,KJ2015B1105906)
【分类号】：TB306;TS176
[Abstract]:The metallized plant fiber non-woven fabric was prepared by PD _ 2 activation combined with electroless nickel plating. By means of X-ray diffraction, scanning electron microscope, four-probe, etc. The effect of electroless plating time on the structure characteristics of nickel coating on the surface of vegetable fiber non-woven fabric was studied. The results show that the crystallization properties of electroless nickel coating on the surface of vegetable fiber nonwoven fabric are improved by prolonging the electroless plating time. When the electroless plating time is 10min, the quality of vegetable fiber nonwoven fabric is 0.038 g / cm ~ 2, and the surface resistivity of the coating is 0.2 惟 cm ~ (2).
【作者单位】： 合肥乐凯科技产业有限公司;合肥学院化学与材料工程系;贺州学院化学与生物工程学院;太原理工大学表面工程研究所;
【基金】：中国科学院能量转换材料重点实验室开放课题基金(KF2016001) 安徽省教育厅一般项目(KJ2015B1105905,KJ2015B1105906)
【分类号】：TB306;TS176
【相似文献】
相关期刊论文 前10条
1 崔升;沈晓冬;肖苏;高志强;;化学镀法制备金属铜包覆纳米碳化硅[J];粉末冶金技术;2008年04期
2 周超兰;张高科;甘慧慧;;化学镀法制备钴包覆碳化硅复合粉末的研究[J];武汉理工大学学报;2011年07期
3 曾高峰;史蕾;徐恒泳;;用化学镀法制备Pd/Ag膜时膜厚和组成的控制[J];催化学报;2009年12期
4 梁胜德,朱时珍,赵振波,钟家湘;化学镀法制备金属/陶瓷复合粉体的特点及应用[J];材料导报;1996年05期
5 陈慕容;贺跃辉;江W，
本文编号：2133080
本文链接：https://www.wllwen.com/kejilunwen/cailiaohuaxuelunwen/2133080.html