薄膜表面装饰工艺参数DOE分析

发布时间：2018-09-11 12:18

【摘要】：基于薄膜表面装饰工艺原理及DSGZ黏弹性本构模型的ABAQUS用户材料子程序,对鼠标外壳贴膜的工艺过程进行仿真分析。分析结果表明,薄膜的厚度最厚为0.200 4 mm,最薄为0.182 1 mm,在X方向上的最大变形量为8.01 mm,在Y方向上的最大变形量为2.939 mm。然后对模外装饰贴膜工艺参数进行DOE分析,分析结果表明,模腔的真空度、常压加压时间、高压加压时间对其厚度的标准偏差具有较大的正效应,高压加压时间对其在X、Y方向变形量的标准偏差也具有很大的正效应。
[Abstract]:Based on the principle of membrane surface decoration and the ABAQUS user material subroutine of DSGZ viscoelastic constitutive model, the process of mouse shell coating was simulated and analyzed. The results show that the thickness of the film is 0.200 4 mm, the thinnest is 0.182 1 mm, the maximum deformation in X direction is 8.01 mm, and the maximum deformation in Y direction is 2.939 mm.. Then, the DOE analysis of the process parameters of the decorative film is carried out. The results show that the vacuum degree of the cavity, the pressure time at normal pressure, and the pressure time at high pressure have a great positive effect on the standard deviation of the thickness of the film. High pressure time also has a great positive effect on the standard deviation of the deformation in the XY direction.
【作者单位】： 华东交通大学交通运输与物流学院;华东交通大学机电与车辆工程学院;
【分类号】：TB306

【相似文献】

相关期刊论文 前10条

1 汤华娟;;科技生产人员的良师益友 工艺设备技术的发展创新——介绍王承遇、陶瑛、谷秀梅编著《玻璃表面装饰(第2版)》[J];玻璃与搪瓷;2010年06期

2 王承遇;姜妍彦;卢琪;庞世红;陶瑛;;我国玻璃表面装饰的现状及发展方向[J];玻璃与搪瓷;2011年01期

3 小池弘之;童连祥;;表面装饰纹设计[J];模具技术;1988年04期

4 刘先曙;钛应用三则[J];稀有金属材料与工程;1990年06期

5 岳新元;糕点表面装饰法[J];烹调知识;1998年01期

6 高大彬;铜表面装饰着色新工艺[J];表面技术;1994年03期

7 王承遇，陶瑛;玻璃表面装饰技术（四）[J];玻璃与搪瓷;1996年02期

8 赵子夫 ,唐利;汉代家具的文化特征 二、动与紧[J];家具与环境;1994年01期

9 ;塑料制品表面装饰技术的发展趋势[J];化工文摘;2001年03期

10 官冬玲;;简析木质材料表面装饰的绿色化[J];才智;2010年35期

相关会议论文 前2条

1 王承遇;姜妍彦;卢琪;庞世红;陶瑛;;我国玻璃表面装饰的现状及发展方向[A];2010全国玻璃技术交流研讨会论文集[C];2010年

2 唐丁宁;;表面装饰工艺研究的现状和展望[A];中国电子学会生产技术学会计算机数控技术研讨会论文集[C];1990年

相关博士学位论文 前1条

1 苏润洲;木质材料表面装饰用材的光致变色机理的研究[D];东北林业大学;2011年

相关硕士学位论文 前1条

1 姚杰;薄膜表面装饰模外成型装备研究[D];浙江工业大学;2015年

，

本文编号：2236667