聚脲金属基复合结构在低速冲击下的动态响应研究

发布时间：2018-10-04 21:15

【摘要】：为探讨聚脲金属复合结构在低速冲击下的动态响应,基于霍普金森杆发射系统驱动圆柱形子弹对聚脲和铝板组成的方形板件,进行了10~17 m/s的低速冲击试验,其中试件包括单一铝板、涂层结构和三明治结构3种配置,并保持了相同的面密度(1.49 g/cm2)。从受冲击面破坏形貌、剩余变形和变形时程等方面对试验结果进行了分析。结果表明,聚脲层涂覆在受冲击侧可以有效缓解有棱冲击体带来的应力集中现象,具有相同面密度的纯铝板结构比背面涂层结构和夹层结构具有更强的抗局部剪切能力和抵抗变形能力。
[Abstract]:In order to investigate the dynamic response of polyurea metal composite structure under low speed impact, a low speed impact test of 10 ~ (17) m / s was carried out on a square plate composed of polyurea and aluminum plate driven by a cylindrical bullet driven by a Hopkinson rod launcher system. The specimen consists of a single aluminum plate, a coating structure and a sandwich structure with the same surface density (1. 49 g/cm2). The experimental results are analyzed from the aspects of the failure morphology, residual deformation and deformation time history of the impact surface. The results show that the polyurea coating on the impacted side can effectively alleviate the stress concentration caused by the impact body with edges. The pure aluminum plate structure with the same surface density has stronger local shear resistance and deformation resistance than the back coating structure and sandwich structure.
【作者单位】： 北京理工大学爆炸科学与技术国家重点实验室;
【分类号】：TB333

【相似文献】

相关期刊论文 前4条

1 黄微波;陈国华;卢敏;张效慈;;聚脲柔性减阻材料的制备及性能[J];高分子材料科学与工程;2007年03期

2 钟萍;廖有为;肖鑫;彭恩高;李健;;聚脲涂层在两种不同摩擦条件下的磨损行为探讨[J];润滑与密封;2008年09期

3 杨保平;席满意;崔锦峰;郭军红;崔卓;;乙二醇改性聚脲微胶囊相变材料的研制[J];应用化工;2014年01期

4 张未来;;各类管道耐磨材料分析及纳米复合聚脲耐磨防腐涂层[J];上海涂料;2009年05期

相关会议论文 前2条

1 林英民;;XW料界“奇葩”——\ 台pc聚脲/奈米}聚脲之m鷫媅A];2010年海峡两岸功能性复合材料论坛论文集[C];2010年

2 林英民;;奈米}聚脲[A];2010年海峡两岸功能性复合材料论坛论文集[C];2010年

相关重要报纸文章 前1条

1 骆林　宋世琦;聚脲研讨会暨秀珀洽谈会成功举行[N];建筑时报;2009年

相关硕士学位论文 前3条

1 韩晓倩;聚酰亚胺-b-聚脲共聚物薄膜的制备研究[D];大连理工大学;2016年

2 吴冲;玻璃纤维/聚脲复合材料的微观结构与力学性能研究[D];哈尔滨工业大学;2013年

3 邸春阳;喷涂型聚氨酯/聚脲耐磨材料的制备及性能研究[D];哈尔滨工程大学;2012年

，

本文编号：2251902