碳酸钙晶须含量对橡胶基摩擦材料性能的影响

发布时间：2018-11-20 10:20

【摘要】：选用碳酸钙晶须作为增强材料,采用半湿法密炼工艺和热压成型法制备了橡胶基摩擦材料,研究了碳酸钙晶须质量分数(0~25%)对摩擦材料硬度、密度、冲击强度、抗拉强度和摩擦磨损性能等的影响。结果表明:随着碳酸钙晶须添加量增加,摩擦材料的硬度、密度、抗拉强度、冲击强度和磨损量均呈下降的趋势;添加碳酸钙晶须的质量分数为15%时,摩擦材料的综合性能最好。
[Abstract]:Using calcium carbonate whisker as reinforcement material, rubber based friction material was prepared by semi-wet mixing process and hot pressing method. The hardness, density and impact strength of friction material were studied by mass fraction of calcium carbonate whisker (0 ~ 25%). Effects of tensile strength and friction and wear properties. The results show that the hardness, density, tensile strength, impact strength and wear of friction materials decrease with the increase of calcium carbonate whisker content. When the mass fraction of calcium carbonate whisker is 15, the friction material has the best comprehensive properties.
【作者单位】： 广西民族大学摩擦材料研究所;北京优材百慕航空器材有限公司;
【基金】：广西自然科学基金资助项目(2014GXNSFAA118332)
【分类号】：TB332

【相似文献】

相关期刊论文 前10条

1 许庆衍;摩擦材料在工作条件下无机和有机组分的变化[J];非金属矿;1981年01期

2 俞佩琛;摩擦材料热影响机理研究综述[J];非金属矿;1983年02期

3 罗一新;工业发达国家摩擦材料发展动态[J];湖南大学邵阳分校学报;1991年01期

4 江世履;摩擦材料标准现状及展望[J];非金属矿;1994年04期

5 ;高性能摩擦材料[J];中国乡镇企业信息;1996年11期

6 新新;蛭石作摩擦材料[J];建材工业信息;1997年10期

7 ;高性能摩擦材料[J];技术与市场;1997年08期

8 张垣,金保宏,付承菊;新型摩擦材料的研究[J];玻璃钢/复合材料;2001年03期

9 刘建秀;曹殿立;宁向可;;机动车用摩擦材料的性能研究[J];煤矿机械;2009年02期

10 汪s，

本文编号：2344645