低温SOFC复合电解质LSGM-碳酸盐的制备及性能

发布时间:2018-01-09 18:14

  本文关键词:低温SOFC复合电解质LSGM-碳酸盐的制备及性能 出处:《稀有金属材料与工程》2017年01期  论文类型:期刊论文


  更多相关文章: 低温固体氧化物燃料电池 LSGM-碳酸盐复合电解质 结构表征 电化学特性


【摘要】:通过固相反应法、甘氨酸-硝酸盐燃烧法和聚丙烯酰胺溶胶凝胶法合成了La_(0.9)Sr_(0.1)Ga_(0.8)Mg_(0.2)O_(2.85)(LSGM)粉体,并与二元碳酸盐复合,制备了低温下具有高离子电导率和良好稳定性的新型LSGM-(Li/Na)_2CO_3复合电解质。研究了LSGM粉体制备方法和二元碳酸盐含量对复合电解质性能的影响。结果表明,LSGM-碳酸盐复合电解质存在电导跃迁温度,且在跃迁温度以上电导率明显提高,600和450℃时分别高达0.122和0.08 S·cm~(-1)。以LSGM-碳酸盐复合物为电解质的单电池表现了良好的性能输出,600和500℃时最高输出功率密度可达617和311 m W·cm~(-2)。同时,电池输出功率和开路电压(OCV)受LSGM形貌、尺寸和碳酸盐含量的影响,以碳酸盐含量为20%(质量分数)的复合物为电解质的单电池性能最佳。
[Abstract]:By solid state reaction. LSGM was synthesized by glycine-nitrate combustion method and polyacrylamide sol-gel method. Powder. And mixed with binary carbonate. A novel LSGM-Li / Na with high ionic conductivity and good stability at low temperature was prepared. The effects of preparation method of LSGM powder and the content of binary carbonate on the properties of composite electrolyte were studied. The conductivity transition temperature of LSGM- carbonate composite electrolyte is higher than that of LSGM- carbonate composite electrolyte. At 600 鈩,

本文编号:1402127

资料下载
论文发表

本文链接:https://www.wllwen.com/kejilunwen/dianlidianqilunwen/1402127.html


Copyright(c)文论论文网All Rights Reserved | 网站地图 |

版权申明:资料由用户f2cec***提供,本站仅收录摘要或目录,作者需要删除请E-mail邮箱bigeng88@qq.com