P3HT与CdTe纳米枝晶p-n异质结敏化ZnO纳米管阵列的光电化学研究
发布时间:2018-03-08 21:10
本文选题:ZnO纳米管 切入点:纳米枝状CdTe 出处:《化学学报》2014年01期 论文类型:期刊论文
【摘要】:采用电化学方法首先在ITO导电玻璃上制备了一维有序ZnO纳米管阵列,然后在ZnO纳米管阵列上采用电化学方法沉积纳米枝状CdTe,形成了纳米枝状CdTe包覆ZnO纳米管的CdTe@ZnO壳核式复合结构,最后在上述复合结构中旋涂一层P3HT薄膜形成P3HT包覆的P3HT@CdTe@ZnO复合薄膜.以此复合薄膜为光活性层组装成半导体敏化太阳电池,研究了该类电池的光电转换性能,对该电池的工作原理进行初步研究,所得太阳电池能量转换效率最高达到1.38%.
[Abstract]:One-dimensional ordered ZnO nanotube arrays were prepared on ITO conductive glass by electrochemical method. Then the nanocrystalline CdTe was deposited on ZnO nanotube array by electrochemical method. The CdTe@ZnO shell core composite structure was formed by nano-dendritic CdTe coated ZnO nanotubes. Finally, P3HT thin films were spin-coated into P3HT films to form P3HT-coated CdTe ZnO composite films. The composite films were assembled as photoactive layers to form semiconductor sensitized solar cells. The working principle of the solar cell is studied. The energy conversion efficiency of the solar cell is as high as 1.38.
【作者单位】: 河北科技大学理学院;
【基金】:国家自然科学基金(Nos.21173065,20573031) 河北省自然科学基金(No.B2010000856) 河北科技大学博士启动基金(QD201050) 校立科研基金(XL201255)资助~~
【分类号】:TM914.4;O614.241
【参考文献】
相关期刊论文 前4条
1 郝彦忠;王伟;;聚3-甲基噻吩修饰硫化物量子点连接纳米结构TiO_2膜的光电化学研究[J];化学学报;2007年06期
2 郝彦忠;马洁霞;孙宝;李英品;任聚杰;;TiO_2纳米棒和CdSe纳米棒复合膜与聚3-甲基噻吩杂化太阳能电池研究[J];化学学报;2010年01期
3 郝彦忠;曹寅虎;孙宝;张彦辉;李英品;徐东升;李香玲;;P3HT/CdS/TiO_2/ZnO一维有序核壳式纳米棒阵列的构制及其在杂化太阳电池中的应用研究[J];化学学报;2012年10期
4 孙宝;郝彦忠;郭奋;李英品;罗冲;裴娟;申世刚;;P3HT修饰一维有序壳核式CdS/ZnO纳米棒阵列复合膜的光电化学性能[J];物理化学学报;2012年12期
【共引文献】
相关期刊论文 前10条
1 张慧;吴t,
本文编号:1585556
本文链接:https://www.wllwen.com/kejilunwen/dianlilw/1585556.html