含NiO的ZnO电阻片五元配方不稳定性及改进途径

发布时间：2018-05-07 21:33

  本文选题：氧化锌电阻片 + 五元配方　； 参考：《电瓷避雷器》2014年06期

【摘要】：针对大批量生产的避雷器产品中有少数产品在出厂前发生直流参考电压降低、0.75倍U1m A下泄漏电流增大的现象,分析其原因:除无纬带的品质不佳和避雷器生产工艺不严格外,主要是含Ni O五元配方的氧化锌电阻片存在热稳定性不好。采取调整电阻片烧成温度曲线、变更电阻片侧面有机釉、调整侧面有机釉固化温度曲线和配制一种新的侧面无机高阻釉的措施后,其热稳定性得到明显改善。
[Abstract]:In view of the phenomenon that the leakage current increases under 0.75 times U1m A before the DC reference voltage is reduced by 0.75 times U1m A in a few of the arrester products produced in large quantities, the reasons are as follows: except for the poor quality of the weft free belt and the lack of strict production technology of the arrester, the reason for the increase of leakage current under the condition of 0.75 times U1m A is analyzed. The main reason is that there is poor thermal stability of zinc oxide resistor with Ni O 5 composition. By adjusting the firing temperature curve of the resistor sheet, changing the side organic glaze, adjusting the curing temperature curve of the side organic glaze and preparing a new side inorganic high resistance glaze, its thermal stability is obviously improved.
【作者单位】： 西安西电高压电瓷有限责任公司;
【分类号】：TM862

【参考文献】

相关期刊论文 前6条

1 郭洁,朱跃;温度对MOA电阻片主要电气性能的影响[J];电瓷避雷器;2002年02期

2 侯清健,徐国跃,赵毅,唐敏;烧结温度和热处理对ZnO压敏陶瓷的影响[J];电瓷避雷器;2004年05期

3 王振林;李盛涛;王玉平;;国外MOA用ZnO电阻片的剖析与思考[J];电瓷避雷器;2007年01期

4 王振林;李盛涛;王玉平;;国外MOA用ZnO电阻片的剖析与思考(续)[J];电瓷避雷器;2007年02期

5 洪秀成;肖汉宁;黄彩清;成茵;;高性能氧化锌电阻片的研究进展[J];电瓷避雷器;2008年03期

6 易月初;郑文斌;陈铁城;;无纬带缠绕芯体的复合外套避雷器质量问题探讨[J];电瓷避雷器;2012年04期

【共引文献】

相关期刊论文 前10条

1 张大卫;施利毅;徐东;吴振红;;ZnO压敏陶瓷烧结工艺优化[J];材料导报;2009年02期

2 祝铭;李玉科;郑嘹赢;程丽红;李国荣;;晶界电性能对ZnO压敏陶瓷性能的影响[J];材料导报;2010年22期

3 李磊;徐政;林枞;孙丹峰;彭虎;;氧化锌压敏电阻微波烧结行为的研究[J];材料科学与工程学报;2006年06期

4 易月初;氧化锌及分散剂性能与氧化锌浆料性能关系的探讨[J];电瓷避雷器;1997年02期

5 马晋华;线路避雷器与绝缘子串间的绝缘配合[J];电瓷避雷器;2000年05期

6 刘勇,骆志新;带热熔式脱离器复合外套避雷器的验证及有关问题的分析[J];电瓷避雷器;2003年03期

7 李盛涛,邹晨,刘辅宜;ZnO压敏陶瓷晶界势垒高度和宽度的研究[J];电瓷避雷器;2004年01期

8 王玉平,李盛涛;化学合成法改进对ZnO压敏电阻片复合粉体的影响[J];电瓷避雷器;2004年06期

9 高奇峰;段雷;;浅析ZnO压敏陶瓷中的气孔产生与预防[J];电瓷避雷器;2011年01期

10 马R，

本文编号：1858544