【摘要】：以苯二甲酸-锌配位化合物(MOF-5)为原料合成金属骨架有机多孔碳MOF-PC,并首次应用于锂空气电池.采用XRD、SEM、TEM、氮气脱吸附和恒流充放电测试研究了MOF-PC的物理及电化学性能.结果表明,样品MOF-PC为无定型碳,比表面积为654m2g-1.以MOF-PC为空气电极的锂空气电池在0.1mA cm-2电流密度下放电比容量高达3 183mA h g-1,比传统碳材料Super P在相同电流密度下的放电比容量高90%.
[Abstract]:Metal skeleton organic porous carbon (MOF-PCS) was synthesized from phthalic acid-zinc coordination compound (MOF-5) and used for lithium air batteries for the first time. The physical and electrochemical properties of MOF-PC were studied by means of XRDX SEMM-TEM, nitrogen desorption and constant current charge-discharge test. The results showed that MOF-PC was amorphous carbon with a specific surface area of 654 m ~ (-2) g ~ (-1). The specific discharge capacity of lithium-air battery with MOF-PC as air electrode is as high as 3 183mA h g -1 at 0.1mA cm-2 current density, which is 90% higher than that of traditional carbon material Super P at the same current density.
【作者单位】： 湘潭大学化学学院 环境友好化学与应用教育部重点实验室;
【基金】：国家自然科学基金项目(51272221,21203161) 湖南省教育厅重点项目(11A118) 湖南省自然科学基金项目(13JJ4501)
【分类号】：O621.3

【参考文献】

相关期刊论文 前1条

1 王先友;魏思伟;舒洪波;吴强;杨秀康;杨顺毅;肖琼;;矿山机车用中等功率型锂离子电池制备技术[J];湘潭大学自然科学学报;2011年01期

【共引文献】

相关期刊论文 前10条

1 李慧;吴川;吴锋;白莹;;超高比能量锂-空气电池最新研究进展[J];稀有金属材料与工程;2014年06期

2 彭佳悦;刘亚利;黄杰;李泓;;锂离子电池基础科学问题(Ⅺ)——锂空气电池与锂硫电池[J];储能科学与技术;2014年05期

3 桑林;徐志彬;丁飞;刘兴江;;锂水电池技术研究进展[J];电源技术;2014年09期

4 卢云;杨春;元杰;宫岩坤;胡永达;;非水系锂空气电池的研究进展[J];电子元件与材料;2014年09期

5 彭丽聪;赵倪婕;陈晓;肖东东;谷林;张志华;;透射电镜表征中锂-氧气电池放电产物的辐照损伤研究[J];电子显微学报;2015年01期

6 罗志虹;赵玉振;郭s，

本文编号：1860550