爆轰法合成纳米磷酸铁锂的性能研究

发布时间：2018-05-11 08:14

  本文选题：爆轰合成 + 磷酸铁锂　； 参考：《工程爆破》2014年06期

【摘要】：由于磷酸铁锂正极材料具有特殊的空间架构以及优越的安全性能、环保性能和其他锂离子电池正极材料无法超越的循环性能,使得其在储能电池和动力电池产业中快速发展。通过配制爆炸合成专用炸药制备了纳米级磷酸铁锂颗粒粉体,分析粉体材料检测结果发现:合成的纳米磷酸铁锂粉体材料的热稳定性比较高,在高温条件下粉体样品的质量维持在一个不变的数值范围内;另外根据扫描得到的伏安曲线发现粉体材料的循环重现性较好,并且材料的脱锂性能与嵌锂性能也具有很好的可逆性。
[Abstract]:Due to the special space structure and superior safety performance of lithium iron phosphate cathode material, environmental protection performance and other lithium ion battery cathode materials can not surpass the cycle performance, which makes it develop rapidly in energy storage battery and power battery industry. Nano-sized lithium-ferric phosphate powder was prepared by preparing a special explosive for explosive synthesis. The test results of the powder material showed that the thermal stability of the synthesized nano-lithium ferric phosphate powder was relatively high. At high temperature, the mass of the powder sample remains within a constant numerical range, in addition, according to the voltammetric curve obtained by scanning, it is found that the reproducibility of the powder material is good. The properties of lithium removal and lithium intercalation also have good reversibility.
【作者单位】： 中国工程爆破协会;
【分类号】：TQ131.11;TM912

【参考文献】

相关期刊论文 前4条

1 陈权，，恽寿榕;爆轰合成超细金刚石机理探讨[J];爆炸与冲击;1996年04期

2 黄学杰;锂离子电池正极材料磷酸铁锂研究进展[J];电池工业;2004年04期

3 李晓杰;李瑞勇;曲艳东;谢兴华;陈涛;;爆轰法合成纳米α-Al_2O_3粉体[J];工程爆破;2006年01期

4 王小红;李晓杰;闫鸿浩;江德安;杜云艳;;乳化炸药密度与纳米MnFe_2O_4颗粒爆炸合成[J];工程爆破;2009年03期

【共引文献】

相关期刊论文 前10条

1 谭婷婷;张淑珍;赵业军;;钛白副产硫酸亚铁制备铁系超细材料的研究进展[J];安徽化工;2011年03期

2 祝明水;胡美娥;龙新平;蒋小华;;含能材料爆燃快速合成氮化硼的初步研究[J];爆炸与冲击;2006年04期

3 胡成林;代建清;戴永年;易惠华;;Ti离子掺杂对LiFePO_4材料性能的影响[J];材料导报;2007年07期

4 韩

本文编号：1873167