VRLA电池AGM隔板性能测试方法讨论

发布时间：2018-12-14 03:53

【摘要】：按JB/T7630.1对4种隔板样品进行厚度、定量、孔率、最大孔径、吸酸值和拉伸强度等测试,重点观察隔板的微观玻璃纤维结构,对比表面积、针刺强度、压缩性和回弹性、弹性疲劳等进行分析。含短切纤维多的隔板,比表面积波动较大,拉伸强度和穿刺强度最小,压缩性和回弹性最差,在高温下易发生弹性疲劳;细纤维含量高的隔板综合性能较佳。
[Abstract]:The thickness, quantity, porosity, maximum pore size, acid absorption value and tensile strength of four kinds of diaphragm samples were measured according to JB/T7630.1. The microstructure, specific surface area, needle punching strength, compressibility and elasticity of the diaphragm were observed. Elastic fatigue, etc. The diaphragm with short cut fiber has a large fluctuation of specific surface area, minimum tensile strength and puncture strength, and the worst compressibility and resilience, and is prone to elastic fatigue at high temperature, and the partition with high fiber content has better comprehensive properties.
【作者单位】： 浙江南都电源动力股份公司;
【分类号】：TM912.1

【参考文献】

相关期刊论文 前5条

1 陈体衔,郑君铣,张瑞恩;电池装配压力对玻璃纤维隔膜的影响[J];蓄电池;1996年02期

2 李福昭;铅酸蓄电池隔板的现状与发展[J];电池;1996年05期

3 华寿南,阎新华,马建平;铅酸蓄电池发展前瞻——第8届欧洲铅酸蓄电池会议的热点问题评介(下)[J];电池;2004年01期

4 孙伟;超细玻璃棉隔板(AGM)比表面积计算公式推导[J];玻璃纤维;1998年06期

5 林长锋;;浅析无碱与中碱玻璃纤维异同[J];21世纪建筑材料;2009年01期

【共引文献】

相关期刊论文 前4条

1 朱雯娟;李卓球;;ECR和中碱玻璃纤维的耐酸性试验[J];玻璃纤维;2010年04期

2 宿占寰;阀控式铅酸蓄电池早期失效的原因分析[J];蓄电池;1997年04期

3 华寿南,朱教伟,王平;VRLA电池的AGM隔板和氧传输(1)[J];电池;2005年02期

4 包有富,张华,胡信国;AGM隔板性能对密封铅酸蓄电池性能的影响[J];电源技术;2000年05期

相关硕士学位论文 前3条

1 黄明香;汽车起动用铅酸蓄电池极板化成及其性能的研究[D];福州大学;2006年

2 李石;新型电动自行车用铅酸蓄电池正极板栅合金的研究[D];华南师范大学;2007年

3 杨晓娟;超高分子量聚乙烯电池膜成型研究[D];北京化工大学;2012年

【二级参考文献】

相关期刊论文 前4条

1 吴永坤,龚方红,沙德仁;纤维玻璃耐碱性的研究[J];玻璃纤维;2004年04期

2 马素卿;日本小型密封铅酸蓄电池用隔板的改进[J];蓄电池;1991年01期

3 张维维;隔板结构对阀控式电池性能的影响[J];蓄电池;1994年04期

4 华寿南,阎新华,马建平;第8届欧洲铅蓄电池会议(8ELBC)回顾[J];蓄电池;2003年02期

，

本文编号：2377869