高温下液硅的润湿性

发布时间：2018-01-05 06:16

本文关键词：高温下液硅的润湿性　出处：《材料科学与工程学报》2017年02期 　论文类型：期刊论文

【摘要】：液硅在耐高温材料上的润湿性对于低成本太阳能电池生产过程中硅的精炼和铸造具有重要的研究意义。为了研究液硅的润湿性,采用座滴法分别研究真空和氩气气氛以及不同温度条件下液硅在高纯石墨以及刚玉基底材料上的接触角。实验结果表明,高纯石墨基底材料表面越粗糙,液硅所形成的接触角越小,从而润湿性越好;真空条件下液硅在刚玉上的接触角并没有随着加热温度的上升呈现下降的趋势,而是在88°~90°的范围内波动,分析图像的过程中可明显看到液硅在刚玉基底材料上左右来回蠕动的现象。
[Abstract]:The wettability of liquid silicon on high temperature resistant materials is of great significance for the refining and casting of silicon in the production of low cost solar cells, in order to study the wettability of liquid silicon. The contact angles of liquid silicon on high purity graphite and corundum substrates were studied by drop method in vacuum and argon atmosphere and at different temperatures. The experimental results show that the surface of high purity graphite substrate is rougher. The smaller the contact angle of liquid silicon is, the better the wettability is. Under vacuum condition, the contact angle of liquid silicon on corundum does not decrease with the increase of heating temperature, but fluctuates in the range of 88 掳~ 90 掳. In the process of image analysis, the phenomenon of liquid silicon creeping back and forth on corundum substrate can be seen obviously.
【作者单位】：常州大学材料科学与工程学院江苏省光伏科学与工程协同创新中心;江苏省光伏科学与技术国家重点实验室培育建设点;
【基金】：国家自然科学基金重点资助项目(51335002) 江苏省优势学科建设工程资助项目江苏省高校青蓝工程资助项目
【分类号】：TN304.12
【正文快照】： 1引言在高温材料科学与工程的许多领域,液态金属-陶瓷系统的润湿性是一个关键要素[1-2]。单晶硅和多晶硅的生产中,采用的方法主要为传统的Czochralski(CZ)法以及连续铸锭法[3]。另外还出现了如限边喂膜法[4]、硅蹼法[5]、横向拉膜法[6]等新型晶硅生产方法。生产中与高温液硅接

【相似文献】