具有不同微观形貌ZnO的控制合成及其气敏性能研究

发布时间：2018-10-05 16:27

【摘要】：利用不同湿化学法制备了具有丰富微观形貌的纳米ZnO,研究了不同制备条件对ZnO形貌的影响,结果表明反应体系过饱和度及压力对所得材料的微观形貌均有较大的影响;系统测试了基于不同微观形貌ZnO气敏元件对丙酮和乙醇气体的敏感性能,结果显示基于棒状连排微观形貌ZnO的气敏元件,其性能最佳。
[Abstract]:Nanocrystalline ZnO, with rich micro-morphology was prepared by different wet chemical methods. The effects of different preparation conditions on the morphology of ZnO were studied. The results show that the supersaturation and pressure of reaction system have great influence on the micromorphology of the obtained materials. The sensitivity of ZnO gas sensor to acetone and ethanol gas based on different microcosmic morphology was systematically tested. The results showed that the gas sensor based on rod-like continuous row micro morphology ZnO had the best performance.
【作者单位】： 阜阳师范学院;湖南大学;喷射沉积技术及应用湖南省重点实验室;
【基金】：国家自然科学基金资助(61404046) 国家青年自然科学基金(21401024) 安徽省自然科学基金面上项目(1508085MB21) 安徽省高校自然科学研究重点项目(KJ2016A550) 阜阳师范学院重大科技成果孵化基金项目(kjfh201606) 安徽省科技攻关计划项目(1301042112) 省级科研机构校级委托专项课题(2014HJJC02) 安徽高校省级自然科学研究一般项目(2015KJ001,2015KJ005)
【分类号】：TN304.21

【相似文献】

相关期刊论文 前4条

1 莫艳,王德君,周济,李龙土,桂治轮;(Sr,Pb)TiO_3陶瓷的半导特性与微观结构的研究[J];压电与声光;1998年04期

2 朱银莲,张明,马秀良,李斗星;La_(1-x)Sr_xMnO_3(x=0.1,0.2,0.3)薄膜的微观结构[J];电子显微学报;2004年04期

3 谷岩;刘心宇;袁昌来;刘俊涛;;SrFe_xSn_(1-x)O_(3-δ)陶瓷材料的微观结构和NTC特性[J];电子元件与材料;2009年09期

4 ;材料[J];电子科技文摘;1999年07期

相关会议论文 前2条

1 鲁燕萍;张云鹤;;含钛衰减陶瓷制作工艺[A];2002年电子陶瓷及其在真空电子行业中应用技术交流会论文集[C];2002年

2 任晓堂;王忠义;于金祥;;共掺氧对铒在硅中微观结构的影响[A];2004全国荷电粒子源、粒子束学术会议论文集[C];2004年

，

本文编号：2254070