电镀锌板钼酸盐体系钝化膜的制备和腐蚀性能研究

发布时间：2018-02-03 06:42

  本文关键词： 镀锌板 钼酸盐 钝化 耐蚀性　出处：《热加工工艺》2017年18期 　论文类型：期刊论文

【摘要】：采用钼酸盐作为主成膜物质对电镀锌板进行钝化处理,采用低浓度铬酸盐作为对比试验。用硫酸铜点滴试验、电化学交流阻抗、极化曲线和金相显微镜观察等方法检验膜层的腐蚀性能。结果表明:钼酸盐-硅烷、钼酸盐-硅烷-有机酸复合钝化可有效提高电镀锌层的腐蚀电位,降低腐蚀电流密度,抑制腐蚀的电化学过程,所以提高了镀锌板的耐腐蚀性,而且比低浓度铬酸盐钝化膜耐蚀性更好。
[Abstract]:Molybdate was used as the main film-forming material to passivate the zinc plating plate, the low concentration chromate was used as the contrast test, the copper sulfate drop test was used, and the electrochemical AC impedance was obtained. Polarization curves and metallographic microscopy were used to examine the corrosion properties of the coatings. The results showed that the composite passivation of molybdate-silane and molybdate-silane-organic acid could effectively increase the corrosion potential of the electroplated zinc coating. The corrosion resistance of galvanized sheet is improved by reducing the corrosion current density and inhibiting the electrochemical process of corrosion, and the corrosion resistance is better than that of low concentration chromate passivation film.
【作者单位】： 太原工业学院化学与化工系;
【基金】：太原工业学院院基金资助项目(2014LY02)
【分类号】：TQ153
【正文快照】： 电镀锌板在机械、汽车、建筑等领域应用十分广泛,但是锌在潮湿的大气中尤其在有氯化物等腐蚀介质存在的条件下,表面很易被腐蚀,影响其外观和使用寿命。因此,电镀锌板通常要进行钝化处理提高其表面的耐蚀性。传统的镀锌板钝化方法是铬酸盐钝化,但该钝化工艺过程中产生的废水及

【相似文献】

相关期刊论文 前10条

1 张文钲;;钼酸盐及其应用研究最近动向[J];钼业经济技术;1991年04期

2 丁益;方辉;;钼酸盐的制备及在催化中的应用[J];化学通报;2014年04期

3 陆柱;;冷却水新型缓蚀剂—杂多钼酸盐的初步研究[J];化肥工业;1980年02期

4 黄希俊;六氯钼酸铝及其衍生物的制备[J];化学试剂;1998年04期

5 方景礼，，刘琴，韩克平，陈耀辉;铝上金黄色钼酸盐电沉积膜的研究[J];电镀与涂饰;1994年04期

6 诸震鸣;;钼酸盐在转化膜处理中的应用[J];材料保护;1993年07期

7 吕建;吴海江;;热锌镀层钼酸盐钝化膜的电子能谱分析[J];装备环境工程;2007年04期

8 牟世辉;;镀锌层钼酸盐钝化工艺研究[J];电镀与精饰;2009年04期

9 刘小虹,颜肖慈;镀锌层钼酸盐转化膜及其耐蚀机理[J];电镀与环保;2002年06期

10 郝建军;安成强;刘常升;;不同添加剂对镀锌层钼酸盐钝化膜腐蚀电化学性能的影响[J];材料保护;2006年10期

相关硕士学位论文 前3条

1 杨星星;多功能稀土掺杂钼酸盐材料的制备及荧光特性研究[D];吉林大学;2016年

2 刘英;稀土钨钼酸盐的制备、结构与性能研究[D];中南大学;2012年

3 刘策;纳米稀土钨/钼酸盐红色荧光粉的制备与表征[D];长春理工大学;2012年

本文编号：1486718