四硼酸钠对Ni-Co合金镀层的影响

发布时间：2018-02-23 17:21

  本文关键词： Ni-Co合金镀层 四硼酸钠 硬度　出处：《电镀与精饰》2016年06期 　论文类型：期刊论文

【摘要】：为提高Ni-Co合金镀层硬度,采用单因素实验研究四硼酸钠对Ni-Co合金镀层硬度的影响,利用硬度测试考察Ni-Co合金镀层硬度的变化,采用金相显微镜对镀层微观形貌进行分析,通过X-射线衍射及能谱分析镀层的相组成和成分,采用电化学测试考察复合镀层耐蚀性。结果表明,当溶液中加入四硼酸钠时,Ni-Co合金镀层中的镍、钴发生变化,镍增加,钴减低,当四硼酸钠为15 g/L时镀层晶粒更加细致,外观表面更加光亮,镀层表面形貌达到最佳;腐蚀电流为9.422μA,硬度达到467.4 HV。
[Abstract]:In order to improve the hardness of Ni-Co alloy coating, the effect of sodium tetraborate on the hardness of Ni-Co alloy coating was studied by single factor experiment. The changes of hardness of Ni-Co alloy coating were investigated by hardness test, and the microstructure of the coating was analyzed by metallographic microscope. The phase composition and composition of the coating were analyzed by X-ray diffraction and energy dispersive spectroscopy. The corrosion resistance of the composite coating was investigated by electrochemical test. The results showed that when sodium tetraborate was added into the solution, the nickel and cobalt in the Ni-Co alloy coating changed and the nickel increased. With the decrease of cobalt, when sodium tetraborate is 15 g / L, the coating grain is finer, the appearance surface is brighter, the surface morphology of the coating is the best, and the corrosion current is 9.422 渭 A, the hardness is 467.4 HV, the corrosion current is 9.422 渭 A and the hardness is 467.4 HV.
【作者单位】： 沈阳理工大学环境与化学工程学院;中国科学院新疆理化技术研究所环境科学与技术研发室;
【分类号】：TQ153.2

【相似文献】

相关期刊论文 前10条

1 谢;;润面油[J];陕西化工;1986年01期

2 杨景广;四硼酸钠在双金属铸造中的应用[J];现代铸铁;1989年01期

3 赵彤;;装饰型浮雕玻璃的生产[J];建材工业信息;1988年21期

4 魏永刚;邹曼逊;;甜莱施用硼肥效果简报[J];甜菜糖业;1987年03期

5 李艺明;叶巧明;;四硼酸钠对水玻璃改性作用的研究[J];广东微量元素科学;2006年10期

6 凌星中,汪素卿;应用四硼酸钠在磷酸钙沉积试验中稳定pH值的研究[J];工业水处理;1990年02期

7 崔德松;;碳酸钠-四硼酸钠碱熔-电感耦合等离子体发射光谱法测定铬铁矿石中11种元素[J];岩矿测试;2012年01期

8 ;广用水溶型防火剂的配制和使用[J];内江科技;1998年02期

9 苏茂尧，，王双一，董思民;两种微交联羧甲基纤维素的结构和性能研究[J];油田化学;1999年01期

10 闻向东;文斌;张穗忠;;GB/T6730.63执行中若干问题的探讨[J];武钢技术;2009年02期

相关会议论文 前1条

1 卢衡;;抗菌剂四硼酸钠对浸渍木质文物的副作用分析[A];中国文物保护技术协会第二届学术年会论文集[C];2002年

本文编号：1526953