不同养护条件对大掺量粉煤灰混凝土抗碳化性能试验研究

发布时间：2018-03-04 16:18

  本文选题：养护条件　切入点：大掺量粉煤灰混凝土　出处：《硅酸盐通报》2017年08期 　论文类型：期刊论文

【摘要】：通过加速碳化试验,系统研究了不同养护条件和粉煤灰掺量的大掺量粉煤灰混凝土碳化规律。并利用扫描电镜和压汞法研究了大掺量粉煤灰混凝土碳化前后的微观形貌和孔结构变化。结果表明:经标准养护后的粉煤灰混凝土的抗碳化能力大于经自然养护后的粉煤灰混凝土的抗碳化能力;随着粉煤灰掺量的增加,混凝土抗碳化能力减小;标准养护下粉煤灰混凝土孔隙率相比于其在自然养护下的孔隙率降低了19.6%;碳化后浆体密实度增加,孔径细化,孔隙率降低31.4%。
[Abstract]:By accelerating the carbonation test, The carbonation law of high content fly ash concrete with different curing conditions and fly ash content was studied systematically, and the microstructure and pore structure of fly ash concrete before and after carbonization were studied by SEM and mercury injection method. The results show that the carbonation resistance of fly ash concrete treated by standard curing is higher than that of fly ash concrete after natural curing. With the increase of fly ash content, the carbonation resistance of concrete decreases; the porosity of fly ash concrete under standard curing decreases 19.6than that under natural curing; the density of slurry increases after carbonization, the pore size is refined, and the porosity decreases 31.4%.
【作者单位】： 潍坊科技学院;
【分类号】：TU528

【相似文献】

相关期刊论文 前7条

1 余春春;舒志坚;;养护条件对混凝土成熟度的影响[J];山西建筑;2011年14期

2 董国勇;;底模和养护条件对砂浆强度影响的对比试验研究[J];山西建筑;2014年01期

3 彭程纬;郭文瑛;杨铮;彭启冬;陈彬彬;杨医博;王恒昌;;养护条件对普通预拌砂浆专用水泥黏结强度影响的研究[J];混凝土;2013年02期

4 杨牧;陈芳斌;秦鸿根;;不同养护条件对净浆微观结构与水化产物的影响[J];混凝土世界;2013年12期

5 田文玉;唐伯明;王国安;;用比强度指标分析养护条件对磨细锶渣活性效应的影响[J];中外公路;2008年06期

6 刘金星;李志强;张荣新;;浅谈养护条件对混凝土强度及耐久性的影响[J];膨胀剂与膨胀混凝土;2007年02期

7 李方元;唐新军;胡小虎;;短龄期养护条件下不同混凝土长期抗硫酸盐侵蚀性能对比[J];粉煤灰综合利用;2013年04期

相关会议论文 前2条

1 林欢;陈文超;蓝垂林;王阵地;王玲;高春勇;张萍;;养护条件对混凝土强度及介观孔结构的影响[A];2013年混凝土与水泥制品学术讨论会论文集[C];2013年

2 黄颖星;严生;蔡安兰;邓敏;;养护条件对水泥砂浆干缩性能的影响[A];第九届全国水泥和混凝土化学及应用技术会议论文汇编（上卷）[C];2005年

相关硕士学位论文 前1条

1 程宝娟;养护条件对混凝土毛细吸水性能影响规律的试验研究[D];大连理工大学;2016年

，

本文编号：1566402