利用中国红花岗石边角料生产无机人造石

发布时间：2018-03-09 10:00

  本文选题：中国红花岗石　切入点：边角料　出处：《中国矿业》2017年08期 　论文类型：期刊论文

【摘要】：本文对利用红色花岗石边角料为骨料,以无机胶凝材料作为胶结料,并配以红色无机颜料及其他外加剂,生产红色人造石进行了研究。结果显示,制品养护至28d时的抗压强度为92.8 MPa,抗折强度为11.9 MPa,吸水率为3.46%,光泽度为63.8光泽单位,其性能超过国家建材行业标准《建筑装饰用水磨石——水泥人造石》(JC/T507—2012)的指标。放射性属于国家标准的A类装饰装修材料,产销和使用范围不受限制。
[Abstract]:This paper studies the production of red artificial stone with red granite scrap as aggregate, inorganic cementitious material as cementing material, red inorganic pigment and other admixtures. The compressive strength, flexural strength, water absorption and glossiness of the products are 92.8 MPa, 11.9 MPA, 3.46 and 63.8 units of luster when they are maintained until 28 days, Its performance exceeds the national standard of building materials industry < Terrazzo for Building Decoration & cement artificial Stone > JC / T507-2012). The radioactive materials belong to the National Standard A for decoration and decoration, and the range of production, marketing and use are not restricted.
【作者单位】： 西南科技大学环境与资源学院;固体废物处理与资源化教育部重点实验室;
【基金】：国家级大学生创新创业训练计划资助(编号:201610619022)
【分类号】：TQ177.17

【相似文献】

相关期刊论文 前10条

1 石汇玉;对人造石实体面材发展的建议[J];新型建筑材料;2001年11期

2 石汇玉;人造石 大有可为[J];中国建材;2002年11期

3 ;人造石国家标准即将公布[J];建材发展导向;2012年02期

4 韩云樵;;人造石棉绒简介[J];氯碱工业;1991年04期

5 ;第二代人造石“丽洁石”[J];技术与市场;2001年11期

6 谭金华;;不卖产品 展示功能 营销空间 提供服务——广东佛山新中源集团万峰人造石的市场经营之道[J];石材;2008年07期

7 马文杰;具有使用性能高、耐光老化和大气老化的人造石材料用的稳定剂体系Т.я.Ко лъ чоВА等[J];合成材料老化与应用;1994年02期

8 徐铮,徐文寿;树脂基人造石[J];化学建材;1999年03期

9 易桢;我国人造石实体面材行业发展战略思考[J];企业技术开发;2004年08期

10 袁淮洲;树脂基人造石及其应用[J];玻璃钢/复合材料;2002年05期

相关重要报纸文章 前1条

1 雨立;人造石产业走入转型陶企新视野[N];中国建材报;2008年

相关硕士学位论文 前1条

1 吴晓鹏;负离子型功能人造石研究[D];华南理工大学;2012年

，

本文编号：1588048