蒸养条件下两性聚羧酸减水剂对胶砂及混凝土强度的影响

发布时间：2018-03-09 22:12

  本文选题：两性型聚羧酸减水剂　切入点：蒸汽养护　出处：《硅酸盐通报》2017年07期 　论文类型：期刊论文

【摘要】：合成了阴离子型和两性型聚羧酸减水剂,研究了两类聚羧酸减水剂对水泥水化热、蒸养胶砂和蒸养混凝土强度的影响。结果表明:在蒸养条件下,与阴离子型聚羧酸减水剂相比,掺两性型聚羧酸减水剂的水泥水化温峰更高;在相同水灰比时,掺两性聚羧酸减水剂的蒸养胶砂和蒸养混凝土的强度也更高。XRD分析可知,掺入两性聚羧酸减水剂在蒸养条件下生成更多的AFm和氢氧化钙,促进了C_3S和C_2S的水化。
[Abstract]:Anion and amphoteric polycarboxylic acid superplasticizers were synthesized. The effects of two kinds of polycarboxylic acid water reducers on the strength of cement hydration heat, steam curing cement sand and steaming concrete were studied. Compared with anionic polycarboxylic acid superplasticizer, the hydration temperature peak of cement mixed with amphoteric polycarboxylic acid superplasticizer is higher than that of anionic polycarboxylic acid superplasticizer, and the strength of steaming cement sand and steaming concrete with amphoteric polycarboxylic acid superplasticizer is higher than that of amphoteric polycarboxylic acid superplasticizer at the same water-cement ratio. The addition of amphoteric polycarboxylic acid superplasticizer to produce more AFm and calcium hydroxide promoted the hydration of C _ 3s and C _ 2S.
【作者单位】： 西安建筑科技大学材料与矿资学院;陕西科之杰新材料有限公司;
【基金】：陕西省社会发展科技攻关项目(2016SF-443)
【分类号】：TU528

【参考文献】

相关期刊论文 前6条

1 董思勤;刘加平;冉千平;杨勇;;两性聚羧酸侧链结构对水泥浆体早期性能的影响[J];新型建筑材料;2015年01期

2 房福贤;杨霞;张鑫;周普玉;郭清春;杨晓晨;周南南;;C80管桩免压蒸工艺研究[J];新型建筑材料;2015年01期

3 肖茜;伍勇华;南峰;何廷树;李论;;蒸养条件下不同种类外加剂对水泥水化进程的影响[J];硅酸盐通报;2013年06期

4 何志旗;伍勇华;南峰;何廷树;;聚羧酸高效减水剂对胶砂蒸养强度的影响[J];混凝土与水泥制品;2011年09期

5 冉千平;刘加平;缪昌文;吴石山;沈健;;两性接枝共聚物超塑化剂对水泥早期水化的影响[J];建筑材料学报;2007年05期

6 蒋元海,匡红杰;石屑在PHC管桩生产中的开发应用[J];建筑技术;2002年01期

【共引文献】

相关期刊论文 前10条

1 伍勇华;张鹏;程浩;陈畅;杨浩;杨颖刚;;蒸养条件下两性聚羧酸减水剂对胶砂及混凝土强度的影响[J];硅酸盐通报;2017年07期

2 赵鹏飞;廖国胜;杨海波;;PHC管桩混凝土全免压蒸制备工艺研究[J];新型建筑材料;2017年02期

3 伍勇华;程浩;张鹏;陈畅;杨浩;杨颖刚;余抗建;;阳离子单体对聚羧酸减水剂早强性能的影响[J];硅酸盐通报;2017年02期

4 陈宝t，

本文编号：1590492