湿法工艺从氧化锰尾矿中回收碳酸锰

发布时间：2018-03-12 23:15

  本文选题：氧化锰尾矿　切入点：SO　出处：《有色金属(冶炼部分)》2017年05期 　论文类型：期刊论文

【摘要】：在硫酸溶液中,以SO_2为还原剂对氧化锰尾矿进行还原浸出,浸出液净化后与碳酸氢铵发生沉淀反应回收碳酸锰。在最优浸出条件下,锰浸出率达96%以上。采用氨水调节pH为5.2时,浸出液中的铁、铝、硅的去除率分别为100%、99.6%和96.9%。净化液与碳酸氢铵反应沉淀率为99.8%,整个工艺锰回收率为90.5%,碳酸锰产品达到《HG/T4203-2011工业碳酸锰》一等品指标要求。
[Abstract]:In sulfuric acid solution, manganese oxide tailings were leached with SO_2 as reducing agent. After purification, precipitation reaction occurred with ammonium bicarbonate to recover manganese carbonate. The leaching rate of manganese is more than 96%. When the pH value of ammonia is adjusted to 5. 2, the iron and aluminum in the leachate can be obtained. The removal rates of silicon were 99.6% and 96.9%, respectively. The precipitation rate of the purified solution reacted with ammonium bicarbonate was 99.8. The recovery rate of manganese carbonate in the whole process was 90.5%, and the manganese carbonate product reached the requirement of the first grade of manganese carbonate in HG/T4203-2011 industry.
【作者单位】： 郑州职业技术学院电气系;中国地质科学院郑州矿产综合利用研究所;
【基金】：国土资源公益性行业科研专项(201211069)
【分类号】：TD926.4;TQ137.12

【相似文献】

相关期刊论文 前10条

1 袁明亮,邱冠周;高纯微晶碳酸锰制备中的粒度和质量控制[J];中南工业大学学报(自然科学版);2001年05期

2 宋士强;;大表面积二氧化锰的制造方法[J];无机盐工业;1980年05期

3 章淑轩;;碳酸锰制备的方法研究[J];化学工程与装备;1985年01期

4 潘万成;高纯碳酸锰的制造方法[J];湖南化工;1989年01期

5 李绪福;;高纯微晶状碳酸锰的研制[J];无机盐工业;1991年04期

6 孟明权,李春英,桑兆昌,贾林平;利用氢醌含锰废渣制取碳酸锰[J];无机盐工业;1994年03期

7 陈书阁;碳酸锰分解氧化工艺条件的探讨[J];无机盐工业;1994年06期

8 钟国清,蒋礼;高纯碳酸锰的制备研究[J];无机盐工业;1996年06期

9 胡修权;孙猛;李桂玲;曹海华;贺爱平;周毅;;超微细碳酸锰合成影响因素控制[J];无机盐工业;2014年01期

10 赵立新,孙来九,郭人民,张小燕,孙宝莲;含锰废水制备高纯碳酸锰除钙的研究[J];无机盐工业;2001年06期

相关硕士学位论文 前2条

1 王俊红;亚微米级碳酸锰和磷酸锰的制备研究[D];南昌大学;2013年

2 李燕灵;高铁菱锰矿制取高纯碳酸锰的实验研究[D];贵州大学;2014年

，

本文编号：1603751