溶蚀混凝土拉伸性能退化的试验研究

发布时间：2018-03-18 10:18

  本文选题：溶蚀混凝土　切入点：溶蚀深度　出处：《混凝土》2017年12期 　论文类型：期刊论文

【摘要】：通过加速试验的方法研究了不同配合比混凝土拉伸力学性能随溶蚀时间的退化规律。在该试验中,主要设计变量包括水灰比和骨料体积含量。试验结果表明,采用酚酞指示剂可以较准确地表征混凝土的溶蚀深度,溶蚀深度近似地与溶蚀时间的平方根成线性关系。混凝土抗拉强度和弹性模量随着溶蚀时间的增长而减小,而峰值应变则随着溶蚀时间的增长而增大。采用合适的水灰比和骨料体积含量,可以减慢溶蚀速率,减轻混凝土拉伸性能的退化。相比混凝土弹性模量和抗拉强度,峰值拉伸应变对溶蚀更为敏感。
[Abstract]:The degradation law of tensile mechanical properties of concrete with different mix ratio with corrosion time is studied by accelerated test. In this experiment, the main design variables include water-cement ratio and aggregate volume content. Phenolphthalein indicator can be used to characterize the corrosion depth of concrete accurately. The corrosion depth is approximately linear with the square root of dissolution time. The tensile strength and elastic modulus of concrete decrease with the increase of corrosion time. The peak strain increases with the increase of the corrosion time. The corrosion rate can be slowed down and the degradation of the tensile properties of concrete can be alleviated by using proper water-cement ratio and aggregate volume content, compared with the elastic modulus and tensile strength of concrete. The peak tensile strain is more sensitive to corrosion.
【作者单位】： 浙江工业大学建筑工程学院;浙江省工程结构与防灾减灾技术研究重点实验室;
【基金】：国家自然科学基金(51379188) 浙江省自然科学基金(LY15E090006)
【分类号】：TU528

【相似文献】

相关期刊论文 前6条

1 曾文雄;;新拌水泥混凝土工作性的测试方法[J];广东建材;2006年02期

2 王俊杰;;废弃灰浆在复合砂预拌混凝土中的应用研究[J];商品混凝土;2011年12期

3 周齐权;;橡胶混凝土工作性及力学性能研究[J];福建建材;2011年05期

4 李鸿芳;刘晓红;陈剑雄;;石粉复合渣高性能混凝土工作性研究[J];河南建材;2006年04期

5 杨保旭;;基于砂浆流变性设计混凝土工作性的配合比设计方法在两伊铁路工程中的验证[J];中国建材科技;2010年03期

6 严亮;姜黎黎;;混凝土原材料选用的基本原则[J];现代装饰(理论);2011年12期

相关重要报纸文章 前1条

1 王品伦;石灰精在混凝土中的应用[N];中国建设报;2006年

相关硕士学位论文 前4条

1 罗时勇;混凝土工作性控制技术及评估方法研究[D];东南大学;2015年

2 李世祥;低温升混凝土的温升测试及其性能研究[D];哈尔滨工业大学;2016年

3 廖建勋;低等级粉煤灰改性及其在混凝土中的应用[D];西南科技大学;2016年

4 周小菲;混凝土抗开裂性能的评价方法与影响因素研究[D];清华大学;2011年

，

本文编号：1629160