水煤浆气化炉用氧化铬砖的显微结构研究

发布时间：2018-03-24 18:42

  本文选题：氧化铬砖　切入点：显微结构　出处：《耐火材料》2017年06期

【摘要】：为了更深入地研究水煤浆气化炉用再结合法氧化铬砖的蚀损机制,利用X-Ray荧光仪、场发射扫描电镜和能谱仪研究了使用前后砖样的化学组成和显微结构。原砖是用电熔氧化铬颗粒、氧化铝粉和氧化锆粉经高温烧结制成的,在氧化铬颗粒和氧化铝之间通过固相反应形成(Al2-x,Crx)O_3固溶体;用后残砖的显微结构表征为工作表面形成显量的Al_2O_3-SiO_2-CaO-FeO系玻璃相,反应层的主要反应产物是尖晶石固溶体和一些硅酸盐。砖的蚀损机制主要是液体熔渣冲蚀了工作面上的晶间和粒间结合。
[Abstract]:In order to study the erosion mechanism of recombined chrome oxide brick for coal water slurry gasifier, X-Ray fluorescence instrument was used. The chemical composition and microstructure of brick samples before and after use were studied by field emission scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). The original brick was made of fused chromium oxide particles, alumina powder and zirconia powder sintered at high temperature. The solid solution was formed by solid state reaction between chromium oxide particles and alumina, and the Al_2O_3-SiO_2-CaO-FeO glass phase was characterized by the microstructure of the residual brick. The main reaction products of the reaction layer are spinel solid solution and some silicate.
【作者单位】： 中钢集团洛阳耐火材料研究院有限公司;武汉科技大学;濮耐北京研发中心;
【分类号】：TQ175.7;TQ545

【相似文献】

相关期刊论文 前10条

1 梁志聪;;影响水煤浆气化炉单炉长周期运行因素的分析[J];大氮肥;2012年02期

2 ;水煤浆气化炉炉衬达13050h时[J];化工机械;2001年04期

3 来维亚;德士古水煤浆气化炉耐火衬里介绍[J];大氮肥;1994年06期

4 柯昌明;李有奇;赵继增;李楠;韩兵强;;水煤浆气化炉用高铬耐火材料的研究进展[J];耐火材料;2014年04期

5 赵玉勇;;水煤浆气化炉耐火材料的应用[J];内蒙古石油化工;2009年14期

6 宋林喜,石凯,董海;TEXACO水煤浆气化炉耐火材料的开发和应用[J];煤化工;1999年01期

7 段勤国;刘会林;王丽萍;;水煤浆气化炉用高铬耐火材料[J];耐火材料;2007年05期

8 尹洪基;朱德先;胡飘;张涛;王金相;;高铬砖与煤渣侵蚀反应的初探[J];耐火材料;2010年03期

9 尹洪基;耿可明;石鹏坤;王金相;;还原气氛对高铬砖性能的影响[J];耐火材料;2010年02期

10 桂明玺;水泥窑用无铬砖的现状及其未来[J];国外耐火材料;1999年08期

相关会议论文 前3条

1 曹海洁;李丽萍;徐晓莹;;高铬砖中氧化锆含量的测定[A];第十届中国化学会分析化学年会暨第十届全国原子光谱学术会议论文摘要集[C];2009年

2 周伟;岳月红;康华荣;李燕京;李勇;;新型干法水泥窑高温带用无铬砖的研制及应用[A];第三届全国水泥企业总工程师论坛暨全国水泥企业总工程师联合会年会文集[C];2010年

3 范志辉;徐延庆;耿可明;孙红刚;闫双志;王金相;;添加ZrO_2对高铬砖性能的影响[A];2008年耐火材料学术交流会论文集[C];2008年

，

本文编号：1659551