流量计导压管断裂失效分析

发布时间：2018-04-02 14:13

  本文选题：应力腐蚀　切入点：疲劳　出处：《材料保护》2017年09期

【摘要】：某化工厂工艺管线上的316不锈钢材质的孔板流量计导压管断裂,导致介质泄漏发生火灾。为查明其失效原因,对断裂的仪表管进行成分、硬度、金相、断口形貌和腐蚀产物分析,确认仪表管发生断裂的原因是在安装应力、震动和环境中Cl元素的共同作用下,先发生了应力腐蚀形成裂纹源,裂纹达到门槛值后又以疲劳形式扩展,最终导致开裂。
[Abstract]:The orifice plate Flowmeter tube of 316 stainless steel material on the process pipeline of a chemical plant is broken, which results in the fire of medium leakage.In order to find out the failure reason, the composition, hardness, metallography, fracture appearance and corrosion product of the broken instrument tube are analyzed. It is confirmed that the reason of the fracture of the instrument tube is under the joint action of installation stress, vibration and Cl element in the environment.The crack source is formed by stress corrosion first, the crack reaches the threshold value and then propagates in the form of fatigue, which leads to the crack finally.
【作者单位】： 中国石油独山子石化分公司压力容器检验所;中国石油独山子石化分公司机动处;中石油西部管道公司工程项目管理部;中国石油独山子石化分公司储运联合车间;
【分类号】：TQ056.15

【相似文献】

相关期刊论文 前10条

1 金敏;;《应力腐蚀研究》即将出版[J];南京工业大学学报(自然科学版);1985年01期

2 沈保罗,冯可芹,高升吉;钛合金的应用和应力腐蚀[J];四川化工与腐蚀控制;2000年02期

3 徐国元;应力腐蚀原因及对策浅析[J];精细化工中间体;2001年04期

4 闫凤芹;夏智富;;硫化氢应力腐蚀原理与防护措施[J];炼油与化工;2009年01期

5 于士淋;;氨管道在工程设计中预防应力腐蚀的研究[J];当代化工;2011年09期

6 ;关于催化吸收解吸系统的腐蚀氢渗透和应力腐蚀问题[J];胜利石油化工;1978年02期

7 成长龄;;高压设备的应力腐蚀及防腐措施[J];河南化工;1980年02期

8 李中柱;;压力容器应力腐蚀爆破事故分析[J];山东化工学院学报;1981年01期

9 鲁涛;魏沪兰;;涂漆金属抗硫化氢应力腐蚀的研究[J];井矿盐技术;1981年01期

10 任凌波;;压力容器的应力腐蚀及其防护[J];辽宁化工;1982年04期

相关重要报纸文章 前1条

1 韩明德;九江石化化肥合成氨装置导压管堵漏成功[N];经理日报;2006年

相关硕士学位论文 前4条

1 张杰;18-8系不锈钢管线和法兰腐蚀失效与研究[D];大连理工大学;2016年

2 李国帅;S32168不锈钢在氯离子环境中的应力腐蚀研究[D];山东大学;2013年

3 范士义;00Cr17Ni14MO3钢乙醛精馏塔底接管失效研究[D];大庆石油大学;2006年

4 刘清;波纹管热网加热器失效研究[D];大庆石油学院;2003年

，

本文编号：1700744