相变储能混凝土的动态冲击压缩试验与分析

发布时间：2018-04-03 03:14

  本文选题：相变储能骨料　切入点：硅粉　出处：《科学技术与工程》2017年30期

【摘要】：采用变截面霍普金森压杆试验装置,对相变储能混凝土进行动态冲击压缩试验。相变储能骨料以膨胀珍珠岩为基体材料吸附硬脂酸丁酯制备而成的。对不同掺量的相变储能骨料与硅粉的混凝土进行动态冲击压缩试验。试验结果表明,相变储能骨料的掺加对混凝土的动态抗压强度会产生不利影响,随着掺量的增大相变储能混凝土的动态抗压强度逐渐降低;而硅粉能够提高混凝土的动态抗压强度,掺量在10%~15%之间效果最佳。
[Abstract]:The dynamic impact compression test of phase change energy storage concrete was carried out by using a variable section Hopkinson compression bar test device.Phase change energy storage aggregate was prepared by adsorption of butyl stearate with expanded perlite as substrate.Dynamic impact compression tests were carried out on concrete with different content of phase change energy storage aggregate and silica fume.The experimental results show that the dynamic compressive strength of the concrete will be adversely affected by the addition of the phase change energy storage aggregate, and the dynamic compressive strength of the concrete decreases with the increase of the content of the concrete.Silica fume can improve the dynamic compressive strength of concrete, and the best effect is between 10% and 15%.
【作者单位】： 安徽理工大学矿山地下工程教育部工程研究中心土木建筑学院;
【分类号】：TU528

【相似文献】

相关期刊论文 前3条

1 刘成楼;陈学联;;相变储能保温隔热砂浆的研究与应用[J];中国涂料;2010年05期

2 朱圣晓;胡小芳;;基于GM(1,N)模型的相变储能陶粒粒度分布对导热性能的影响[J];中国粉体技术;2010年04期

3 杨玉山;董发勤;甘四洋;;相变储能混凝土的研究[J];功能材料;2007年02期

相关硕士学位论文 前1条

1 章磊;铝基中高温相变储能材料制备及其物化性能研究[D];成都理工大学;2012年

，

本文编号：1703365