氯氧镁水泥基钼尾矿胶砂的制备

发布时间：2018-04-03 20:23

  本文选题：氯氧镁水泥　切入点：钼尾矿　出处：《新型建筑材料》2017年07期

【摘要】：以氯氧镁水泥为胶凝材料,钼尾矿为细骨料,制备氯氧镁水泥基钼尾矿胶砂试块。研究了氯氧镁溶液组成和钼尾矿掺量对胶砂试块力学性能的影响。结果表明,当氯化镁溶液波美度为26°Bé、掺量为200 ml、m(钼尾矿)∶m(Mg O)=66∶34时,制备的氯氧镁水泥基钼尾矿胶砂28 d抗折和抗压强度分别为5.0、10.7 MPa。
[Abstract]:Magnesium oxychloride cement based molybdenum tailings were prepared by using magnesium oxychloride cement as cementitious material and molybdenum tailings as fine aggregate.The effects of the composition of magnesium oxychloride solution and the content of molybdenum tailings on the mechanical properties of cement sand were studied.The results show that when the wave beauty of magnesium chloride solution is 26 掳B 茅, and the content is 200 ml / m (molybdenum tailings), the bending strength and compressive strength of magnesium oxychloride cement-based molybdenum tailings are 5.0 ~ 10.7 MPa for 28 days, respectively.
【作者单位】： 商洛学院化学工程与现代材料学院陕西省尾矿资源综合利用重点实验室;
【基金】：商洛市科技计划项目(SK2014-01-03) 陕西省尾矿资源综合利用重点实验室开放基金(2014SKY-WK017) 国家级大学生创新创业训练计划项目(201511396707)
【分类号】：TQ177

【相似文献】

相关期刊论文 前10条

1 杨治国;周立霞;张戎令;;粉煤灰粒度分布对其胶砂性能的影响[J];中国建材科技;2011年02期

2 曾尤;卢桂霞;赵丽佳;李秋义;;颗粒整形再生胶砂需水量和强度研究[J];沈阳建筑大学学报(自然科学版);2011年02期

3 ;水泥软练胶砂组成的研究[J];水泥;1974年01期

4 周万良;方坤河;;矿渣掺量对胶砂和混凝土强度的影响[J];硅酸盐通报;2012年02期

5 王立华;陈理达;刘佳;;矿渣和粉煤灰对胶砂力学性能的影响研究[J];广东水利水电;2012年03期

6 赵旭光;赵三银;吴国林;何永刚;文梓芸;;转炉钢渣对矿渣-硅酸盐水泥混合胶砂的收缩补偿效应[J];西安建筑科技大学学报(自然科学版);2006年02期

7 毕亚丽;刘艳;张勇;;粉煤灰和天然火山灰对胶砂性能影响对比试验研究[J];西北水电;2012年01期

8 沈洋,卢都友,许仲梓,唐明述;硅质集料碱活性快速砂浆棒试验方法2.养护碱溶液和砂浆胶砂比与试样膨胀的关系[J];南京化工大学学报(自然科学版);2000年01期

9 李小玲;何廷树;;混凝土搅拌站废水对水泥及胶砂性能影响[J];混凝土;2011年03期

10 杨治国;周立霞;张戎令;;粉煤灰粒度分布对粉煤灰-水泥胶凝体系的影响[J];城市道桥与防洪;2011年06期

相关会议论文 前1条

1 杭美艳;兰英静;王树奇;;不同温度对膨胀剂在胶砂中限制膨胀作用的影响[A];中国建筑材料联合会混凝土外加剂分会第十四次会员代表大会--“科隆杯”混凝土外加剂论文集（下册）[C];2014年

相关硕士学位论文 前3条

1 王彦超;基于分形理论的废玻璃粉胶砂性能的研究[D];南华大学;2015年

2 杨利民;外加剂对胶砂和混凝土收缩性能影响的试验研究[D];西安建筑科技大学;2006年

3 孙丽蕊;再生微粉材性及其对再生制品影响的研究[D];北京建筑工程学院;2012年

，

本文编号：1706768