石墨钢珠复相智能环氧树脂混凝土的拉敏特性研究

发布时间：2018-04-04 10:11

  本文选题：石墨　切入点：钢珠　出处：《硅酸盐通报》2017年08期

【摘要】：土木工程中构件受拉区的变形和裂缝影响其承载力和正常使用,因此研究受拉构件的传感材料有重要意义。本文在环氧树脂混凝土中掺入石墨和钢珠,制成一种新型环氧树脂基混凝土材料,通过改变钢珠掺量,测试试件在单调受拉和循环受拉下的应变-电阻变化关系。试验结果表明,该材料在受拉荷载下具有良好的灵敏度和重复性。若将其作为传感材料运用于构件中,可以对受拉区的变形及裂缝进行有效监测。
[Abstract]:In civil engineering, the deformation and crack in the tensile zone affect the bearing capacity and normal use, so it is of great significance to study the sensing materials of the tensile members.In this paper, a new epoxy resin based concrete material was made by adding graphite and steel beads into epoxy resin concrete. By changing the content of steel beads, the strain-resistance relationship of the specimens under monotone and cyclic tension was tested.The experimental results show that the material has good sensitivity and repeatability under tensile loading.If it is used as a sensing material, it can effectively monitor the deformation and crack in the tensile zone.
【作者单位】： 南京理工大学土木工程系;江苏大学土木工程与力学学院;
【基金】：国家自然科学基金项目(51478209)
【分类号】：TU528

【相似文献】

相关期刊论文 前4条

1 周梅;纪成君;高洪江;;利用粉煤灰制备树脂混凝土的试验研究[J];硅酸盐通报;2005年06期

2 刘海卿;周梅;李敏静;;基于均匀设计和最优化技术的树脂混凝土最优配合比试验研究[J];科学技术与工程;2006年12期

3 周梅;汪振双;焦玉麟;;大掺量煤矸石和粉煤灰制备树脂混凝土的研究[J];山西建筑;2006年14期

4 周梅;汪振双;杨利辉;;废玻璃-粉煤灰制备树脂混凝土的试验研究[J];科学技术与工程;2006年21期

相关硕士学位论文 前1条

1 张园;基于剩余强度理论的树脂混凝土疲劳性能研究[D];南京理工大学;2015年

，

本文编号：1709502