大比表面积大孔体积氧化铝的制备进展

发布时间：2018-04-08 18:02

  本文选题：大比表面积　切入点：大孔体积　出处：《石油化工》2016年03期

【摘要】：综述了大比表面积大孔体积的氧化铝的制备方法及其进展,包括醇铝水解法、热分解法、偏铝酸钠CO2中和法、有机溶剂法、有机模板剂法和无模板剂法等。通过对氧化铝的比表面积和孔体积等性质的讨论,展望了未来大比表面积大孔体积氧化铝的研究方向,指出无模板剂法的合成原料廉价易得、合成方法简便快捷、合成过程绿色环保,是未来发展的方向。
[Abstract]:The preparation and progress of alumina with large specific surface area and large pore volume are reviewed, including hydrolysis of aluminol, thermal decomposition, CO2 neutralization of sodium metaluminate, organic solvent method, organic template method and non-template method, etc.Based on the discussion of specific surface area and pore volume of alumina, the research direction of large specific surface area and large pore volume alumina in the future is prospected. It is pointed out that the synthetic raw materials without template method are cheap and easy to obtain, and the synthesis method is simple and quick.The synthesis process is green and environmental protection, which is the direction of development in the future.
【作者单位】： 北京化工大学化工资源有效利用国家重点实验室;宜春学院物理科学与工程技术学院;
【分类号】：TQ133.1

【相似文献】

相关期刊论文 前9条

1 谭旭杲;徐霖;康顺吉;熊秀章;沈喜洲;;FCC催化剂脱金属处理对孔体积影响的研究[J];化学与生物工程;2008年03期

2 盛景云,王跃敏,方维平;一种新的γ-Al_2O_3制备方法[J];厦门大学学报(自然科学版);2003年05期

3 赵军;张兴凯;王云海;;硫铁矿的比表面积、孔体积及其对硫铁矿吸附能力的影响研究[J];中国安全生产科学技术;2008年04期

4 王平;郁卫飞;张娟;刘春;;超细HNS颗粒状态研究[J];含能材料;2008年05期

5 钟玲文,张慧,员争荣,雷崇利;煤的比表面积 孔体积及其对煤吸附能力的影响[J];煤田地质与勘探;2002年03期

6 揭嘉;王玉林;杨运泉;包建国;刘文英;李国龙;;大孔体积、超高比表面积γ-Al_2O_3的制备与表征[J];石油化工;2008年08期

7 ;国外期刊摘录[J];中国胶粘剂;1995年03期

8 陈长春,寇开昌,林德宽;泡沫塑料开闭孔体积百分率试验装置与方法[J];工程塑料应用;1997年02期

9 ;[J];;年期

相关会议论文 前1条

1 陈长春;冠开昌;林德宽;;泡沫塑料开、闭孔体积百分率测试方法研究[A];中国电子学会生产技术学会工程塑料专业委员会、塑料制件国产化技术研讨会论文集[C];1991年

相关硕士学位论文 前1条

1 孙建川;大比表面积大孔体积薄水铝石的制备与应用[D];北京化工大学;2015年

，

本文编号：1722722