玻璃粉末掺合料的研究与应用

发布时间：2018-05-01 09:02

  本文选题：玻璃粉末 + 掺量　； 参考：《混凝土》2017年11期

【摘要】：废弃玻璃经破碎研磨后具有火山灰活性,将其用作水泥混凝土掺合料具有良好的性能,并且有利于减少二氧化碳的排放。目前国内对此种材料用法研究甚少,国外的研究也较为零散。整理分析了国内外学者的相关研究数据,分析了玻璃粉末掺合料的物理化学特性,研究了该种水泥所制混凝土的力学性能,并分析了掺量,养护龄期和养护温度的影响,得出最佳的玻璃粉末掺合料掺量范围为20%~25%。对于推动国内玻璃粉末掺合料在水泥混凝土中应用具有积极作用。
[Abstract]:The waste glass has pozzolanic activity after crushing and grinding, it has good performance as cement concrete admixture, and it is helpful to reduce carbon dioxide emission. At present, there are few studies on the use of this material in China, and more scattered research abroad. The related research data of domestic and foreign scholars are analyzed, the physical and chemical properties of glass powder admixture are analyzed, the mechanical properties of concrete made by this kind of cement are studied, and the influence of the amount of cement, curing age and curing temperature on the concrete is analyzed. The optimum range of glass powder admixture is 20% 25%. It plays an active role in promoting the application of glass powder admixture in cement concrete.
【作者单位】： 上海交通大学船舶海洋与建筑工程学院;英国伯明翰大学机械与土木工程学院;
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 孙志刚;我国掺合料及掺合料技术现状和展望[J];中国水泥;2004年11期

2 陈建辉;;掺合料在混凝土生产中的应用[J];广东建材;2012年07期

3 刘雅琦;阮炯正;仲崇山;孙英娇;;混凝土矿物复合掺合料应用技术规范的探讨[J];吉林建筑工程学院学报;2013年02期

4 赵学明;张晓平;尹友非;张浦阳;;有掺合料高强、超高强高性能混凝土的试验结果与分析[J];混凝土;2013年06期

5 张德娟;徐虎;郭立伟;刘险峰;;掺加掺合料高强高性能混凝土的材料性能试验研究[J];新疆大学学报(自然科学版);2006年02期

6 刘志国;刘红霞;杨少伟;;水泥掺合料分析对混凝土配合比设计的重要性[J];混凝土;2012年09期

7 钱大行;孙犁;张日华;;再生磨细掺合料的研制和应用[J];混凝土;2008年09期

8 赵国成;牛亚林;李永亮;;绿色复合掺合料在混凝土中的实验与生产应用[J];四川建材;2014年03期

9 袁永福;金高峰;兰燕红;;掺合料在混凝土中最佳组合和影响的试验研究[J];基建优化;2006年01期

10 星武 ,段艳;资中研制成功水泥助磨掺合料[J];内江科技;2003年01期

相关会议论文 前8条

1 向安乐;袁红星;;复合掺合料在预应力高强混凝土管桩生产中的应用[A];中国混凝土与水泥制品协会2012年会论文集[C];2012年

2 张德娟;徐虎;郭立伟;刘险峰;;掺加掺合料高强高性能混凝土的材料性能试验研究[A];全国高性能混凝土和矿物掺合料的研究与工程应用技术交流会论文集[C];2006年

3 沈Z醚，

本文编号：1828637