烧结页岩清水砖抗冻性能研究

发布时间：2018-05-11 11:35

  本文选题：新型建筑材料 + 烧结页岩清水砖　； 参考：《科学技术与工程》2017年07期

【摘要】：广西科技大学新型建筑材料课题组前期试验数据作为理论依据,以烧结页岩砖的原料物理性质为基础,研制开发烧结页岩清水砖。为了进一步研究烧结页岩清水砖的抗冻性能,通过将烧结页岩清水砖与普通烧结页岩砖试件的理化成分与微观结构进行对比分析,再进行冻融循环对比试验,以及砖体在饱水状态下的导热系数测定,得出清水烧结页岩砖抗冻性能要优于普通烧结页岩砖。试验结论为:烧结页岩清水砖抗冻性能达到《墙体材料应用统一技术规范》GB 50574-2010相关指标。为后续试验提供相关数据,为烧结页岩清水砖的推广奠定基础,并建议将饱水状态下的砖体导热系数作为砖体抗冻性能指标之一。
[Abstract]:Based on the experimental data of new building materials in Guangxi University of Science and Technology and the physical properties of sintered shale bricks, the sintered shale-water brick was developed. In order to further study the frost resistance of sintered shale clear water brick, the physical and chemical composition and microstructure of sintered shale clear water brick and ordinary sintered shale brick specimen were compared and analyzed, and then freeze-thaw cycle contrast test was carried out. And the thermal conductivity of sintered shale brick is better than that of ordinary sintered shale brick. The test results show that the frost resistance of sintered shale-clear brick reaches the relevant indexes of GB50574-2010. It is suggested that the thermal conductivity of sintered shale clear water brick should be regarded as one of the indexes of brick frost resistance.
【作者单位】： 广西科技大学土木建筑工程学院;
【基金】：广西千亿元产业重大科技攻关(桂科攻11107021-3-5,桂科攻1099058) 广西科技攻关(桂科攻12100007) 柳州市科技局项目(科技攻关与新产品试制2013J010404) 广西科技厅(桂科攻14126001-4) 广西科技大学研究生教育创新计划(GKYC201630)资助
【分类号】：TU522.1

【相似文献】

相关期刊论文 前3条

1 徐晓虹;熊碧玲;吴建锋;李鹏;佘子伟;邓大侃;;废铝灰制备陶瓷清水砖的研究[J];武汉理工大学学报;2006年05期

2 吴建锋;丁培;徐晓虹;郭全胜;;富赤泥陶瓷清水砖的研制[J];武汉理工大学学报;2007年07期

3 ;[J];;年期

相关会议论文 前1条

1 吴立才;;上海市黄浦区174街坊安培洋行外立面清水砖修复[A];华南地区古村古镇保护与发展（广州）研讨会文集[C];2008年

相关重要报纸文章 前1条

1 中国第十三冶金建设公司 石杨 曹茂祥;建筑与材料的应用[N];山西科技报;2003年

相关硕士学位论文 前5条

1 王东斌;艺术型清水砖的研制[D];武汉理工大学;2005年

2 宫平;装饰清水砖施工工艺改进研究[D];西安建筑科技大学;2016年

3 陈琼;清水砖幕墙系统的探讨[D];浙江大学;2016年

4 钟文波;环保型清水砖的研制[D];武汉理工大学;2005年

5 丁培;系列赤泥质陶瓷清水砖的研究[D];武汉理工大学;2007年

，

本文编号：1873783