氧化银电极对锌银贮备电池激活时间的影响

发布时间：2018-05-30 12:18

  本文选题：氧化银电极 + 锌银贮备电池　； 参考：《电源技术》2017年09期

【摘要】：采用几种化成制度制备了氧化银电极和锌电极,以恒流极化、单体手动激活放电和组合电池自动激活放电实验考察了电极的电性能;采用扫描电子显微镜(SEM)和化学分析对氧化银电极的表面形态和组分进行了表征。结果表明,氧化银电极放电初期极化大是影响电池组激活时间的主要因素,也是造成电池放电初期电压上升缓慢的主要原因,9 m A/cm2转6、3 m A/cm2的阶梯充电模式有利于提高电池激活速度。
[Abstract]:Silver oxide electrode and zinc electrode were prepared by several chemical processes. The electrical properties of the electrode were investigated by constant current polarization, manual activation discharge of monomer and automatic activation discharge of combined battery. The surface morphology and composition of silver oxide electrode were characterized by scanning electron microscopy (SEM) and chemical analysis. The results show that the large polarization in the initial discharge of silver oxide electrode is the main factor affecting the activation time of the battery pack. It is also the main reason that the voltage rise slowly in the initial discharge stage of the battery. The stepwise charging mode of 9 m A/cm2 to 6 m A/cm2 is helpful to improve the activation speed of the battery.
【作者单位】： 中国电子科技集团公司第十八研究所;
【分类号】：TM911

【相似文献】

相关期刊论文 前6条

1 关抗芳;;新法制备银—硫化银电极[J];杭州化工;1983年01期

2 陈胜利，吴秉亮，杨汉西;电化学石英晶体微天平对银电极氧化还原过程的研究[J];高等学校化学学报;1994年01期

3 王琪山,黄秀贞,王瑾;PTC陶瓷欧姆接触银电极的研究[J];电子元件与材料;1993年03期

4 付秀芝,陈玲君,汪葆浚;银电极络合电位法测定镀铬液中SO_4~(2-)的含量[J];华东化工学院学报;1985年03期

5 颜志明;自动电位滴定法测定水中氯离子[J];环境监测管理与技术;1997年02期

6 廖孟生，，吕鑫，张乾二;相对论密度泛函法对CN~－在铜和银电极上振动频率的研究[J];电化学;1995年03期

相关硕士学位论文 前2条

1 王晓春;在金银电极上电解二氧化碳制备一氧化碳的研究[D];昆明理工大学;2015年

2 张永光;贮备式锌—银电池氧化银电极的电化学性能研究[D];哈尔滨工业大学;2011年

本文编号：1955274