电刷镀镍过程中316L不锈钢表面状态的变化

发布时间：2018-06-15 19:56

  本文选题：电刷镀镍 + 表面状态　； 参考：《电镀与涂饰》2017年16期

【摘要】：利用X射线光电子能谱仪(XPS)、扫描电镜(SEM)、能谱仪(EDS)等设备研究了电刷镀镍各步骤对316L不锈钢表面状态的影响。清洗可有效地降低316L不锈钢表面的C含量;活化会对表面造成腐蚀,提高表面粗糙度;预镀镍可以获得仅有较少微裂纹的薄镀层。虽然刷镀镍层表面存在较多微裂纹,但仍可以满足钎焊对厚度、结合力和耐高温性能的要求。
[Abstract]:The effect of nickel plating on the surface state of 316L stainless steel was studied by means of X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and energy spectrometer (EDS). Cleaning can effectively reduce the content of C on the surface of 316L stainless steel, the activation will cause corrosion on the surface and improve the surface roughness, and the thin coating with only less micro-cracks can be obtained by pre-plating nickel. Although there are many micro-cracks on the surface of the brushing nickel coating, it can still meet the requirements of the thickness, adhesion and high temperature resistance of brazing.
【作者单位】： 中国工程物理研究院电子工程研究所;
【基金】：基金项目:电真空用高速镀镍技术研究(S20140802)
【分类号】：TG178;TQ153.12

【相似文献】

相关期刊论文 前10条

1 李新涛;;不锈钢镀银[J];电镀与精饰;1984年06期

2 余碧颜;;泵、阀门和配件用的不锈钢的选择[J];广西化工;1982年01期

3 徐孝峰;忻尚锲;;不锈钢镀黑铬[J];电镀与精饰;1988年03期

4 唐春华;;不锈钢表面处理技术[J];电镀与涂饰;1990年03期

5 邹宽贤, 邵傅;用兰点法检查不锈钢表面钝化膜的质量[J];石油化工设备;1994年06期

6 裴国喜;;铬与不锈钢表面的电刷镀工艺研究[J];电镀与精饰;1985年02期

7 谭琼林;高军;;不锈钢零件电镀锡铈合金[J];材料保护;1990年11期

8 章明;增强不锈钢镀银层结合力的电解活化法[J];电镀与精饰;1996年04期

9 ;不锈钢镀前的活化处理[J];材料保护;1971年03期

10 周红红;不锈钢电镀的预处理[J];电镀与精饰;2001年06期

相关会议论文 前1条

1 李兴彦;黄永章;张新;罗远辉;王力军;;不锈钢表面电镀黑铬的研究[A];第七届中国功能材料及其应用学术会议论文集（第7分册）[C];2010年

相关博士学位论文 前1条

1 鞠鹏飞;316L不锈钢表面电镀钯合金膜层工艺及其在非氧化性介质中耐蚀行为研究[D];北京化工大学;2013年

相关硕士学位论文 前2条

1 付亚波;不锈钢表面多孔换热管制备与传热性能试验研究[D];华东理工大学;2017年

2 吴昌霖;316L不锈钢表面电镀钯镍合金膜层在高温非氧化性介质中的耐蚀性能研究[D];北京化工大学;2013年

，

本文编号：2023385