新拌混凝土坍落度损失影响因素试验分析

发布时间：2018-06-30 18:36

  本文选题：新拌混凝土 + 坍落度损失　； 参考：《水电能源科学》2017年02期

【摘要】：鉴于流变参数与坍落度的关联性,引入流变参数成为量化分析坍落度损失的有效途径。利用正交试验方法分析了浆骨比、减水剂和砂率3种混凝土配合比参数与混凝土拌合状态流变参数(屈服强度和粘度)经时变化及坍落度损失的相互关系,验证了屈服强度和粘度可表征坍落度损失,明确了配合比参数对坍落度损失的影响程度,并确定砂率为44%、减水剂为1.2%、浆骨比为0.42为最合理的配合比。
[Abstract]:In view of the relationship between rheological parameters and slump, the introduction of rheological parameters is an effective way to quantitatively analyze slump loss. By using orthogonal test method, the relationship between three kinds of concrete mixture ratio parameters, mortar ratio, water reducer and sand ratio, and rheological parameters (yield strength and viscosity) in concrete mixing state is analyzed. It is verified that yield strength and viscosity can characterize slump loss, and the influence of mix ratio parameters on slump loss is determined. The sand ratio is 44, the water-reducing agent is 1.2 and the ratio of slurry to bone is 0.42. The optimum mixture ratio is determined as follows: the sand ratio is 44, the water-reducing agent is 1.2 and the ratio of slurry to bone is 0.42.
【作者单位】： 河海大学水利水电学院;
【分类号】：TU528

【相似文献】

相关期刊论文 前6条

1 张冬原;吴永川;刘永奎;;坍落度损失的产生原因及解决措施[J];商品混凝土;2011年08期

2 赵立军;;泵送混凝土坍落度损失原因分析[J];中小企业管理与科技(下旬刊);2011年01期

3 禹化伟;;解决混凝土坍落度损失问题的试验研究[J];科技信息;2012年36期

4 庞燕;;浅谈混凝土坍落度损失原因[J];呼伦贝尔学院学报;2011年06期

5 王金霞;;KL-1型载体流化剂的抑制坍落度损失机理[J];煤炭技术;2013年03期

6 ;[J];;年期

相关会议论文 前1条

1 陈建奎;王栋民;;复合超塑化剂(CSP)对FLC和HPC坍落度损失的控制[A];吴中伟院士从事科教工作六十年学术讨论会论文集[C];2004年

相关硕士学位论文 前1条

1 李胜凯;预拌混凝土坍落度损失规律及控制技术研究[D];河北工业大学;2015年

，

本文编号：2086456