三氧化钼——一种新型有机系钠离子储能器件负极材料
发布时间：2018-07-24 21:26
【摘要】：由于锂资源短缺,我们尝试使用三氧化钼作为钠离子储能装置负极材料。通过一种简单的方法合成了三氧化钼,使用XRD、SEM和TEM等测试手段对其物性进行了表征。利用三氧化钼作为有机系钠离子储能器件的负极材料,通过循环伏安和恒流充放电测试探讨了负极材料的储钠机理。以三氧化钼(MoO3)作为负极材料,活性炭(AC)和石墨(graphite)作为正极材料,组装成新型的电化学储能器件,研究了两种器件在1mol/L NaPF6的碳酸丙烯酯(PC)中的电化学性能。两种器件的电压范围分别为0~3.2V和0~3.5V,能量密度最高可分别达到31.6和53 Wh/kg,长循环性能远远优于AC/AC对称电容器。此种储能装置有望成为锂离子电池的一个很好的替代。
[Abstract]:Due to the shortage of lithium, we try to use molybdenum trioxide as anode material for sodium ion energy storage device. Molybdenum trioxide was synthesized by a simple method. The physical properties of molybdenum trioxide were characterized by XRD SEM and TEM. The mechanism of sodium storage in organic sodium ion storage devices was investigated by cyclic voltammetry and constant current charge-discharge measurements using molybdenum trioxide as negative electrode material. A novel electrochemical energy storage device was fabricated using molybdenum trioxide (MoO3) as negative electrode material and activated carbon (AC) and graphite (graphite) as cathode materials. The electrochemical properties of two kinds of devices in 1mol/L NaPF6 (PC) were studied. The voltage ranges of the two devices are 0 ~ 3.2V and 0 ~ (3. 5) V, respectively. The maximum energy density can reach 31.6 and 53 / kg, respectively. The long cycle performance of the two devices is much better than that of AC/AC symmetrical capacitors. This kind of energy storage device is expected to be a good substitute for lithium ion batteries.
【作者单位】： 辽宁石油化工大学;中国科学院长春应用化学研究所电分析化学国家重点实验室;
【基金】：国家重大科学研究计划(2011CB935702,2012CB932800) 国家自然科学基金(21173206) 辽宁石油化工大学引进人才科研启动基金资助项目(2016XJJ-020)~~
【分类号】：TM912;TQ136.12
本文编号：2142702
[Abstract]:Due to the shortage of lithium, we try to use molybdenum trioxide as anode material for sodium ion energy storage device. Molybdenum trioxide was synthesized by a simple method. The physical properties of molybdenum trioxide were characterized by XRD SEM and TEM. The mechanism of sodium storage in organic sodium ion storage devices was investigated by cyclic voltammetry and constant current charge-discharge measurements using molybdenum trioxide as negative electrode material. A novel electrochemical energy storage device was fabricated using molybdenum trioxide (MoO3) as negative electrode material and activated carbon (AC) and graphite (graphite) as cathode materials. The electrochemical properties of two kinds of devices in 1mol/L NaPF6 (PC) were studied. The voltage ranges of the two devices are 0 ~ 3.2V and 0 ~ (3. 5) V, respectively. The maximum energy density can reach 31.6 and 53 / kg, respectively. The long cycle performance of the two devices is much better than that of AC/AC symmetrical capacitors. This kind of energy storage device is expected to be a good substitute for lithium ion batteries.
【作者单位】： 辽宁石油化工大学;中国科学院长春应用化学研究所电分析化学国家重点实验室;
【基金】：国家重大科学研究计划(2011CB935702,2012CB932800) 国家自然科学基金(21173206) 辽宁石油化工大学引进人才科研启动基金资助项目(2016XJJ-020)~~
【分类号】：TM912;TQ136.12
【相似文献】
相关期刊论文 前1条
1 李峰;杨全红;;序[J];新型炭材料;2014年04期
相关会议论文 前4条
1 智林杰;;基于石墨烯的富碳纳米材料及其在储能器件中的应用[A];2011中国材料研讨会论文摘要集[C];2011年
2 邓正华;王璐;李仁贵;侯敏;陈勉忠;刘力;魏晋;张晓正;;一种新型的腈基微孔聚合物膜及其在储能器件中的应用[A];第十二届中国固态离子学学术会议论文集[C];2004年
3 邓正华;王璐;李仁贵;侯敏;陈勉忠;刘力;魏晋;张晓正;;一种新型的腈基微孔聚合物膜及其在储能器件中的应用[A];2004年中国材料研讨会论文摘要集[C];2004年
4 麦立强;赵康宁;牛朝江;晏梦雨;;纳米线电化学储能器件[A];中国化学会第29届学术年会摘要集——第24分会：化学电源[C];2014年
相关博士学位论文 前3条
1 侯建华;多孔碳的结构设计及其电化学储能性能研究[D];北京理工大学;2015年
2 许恒辉;一维电极材料的构筑及其在电化学储能器件中的应用[D];华中科技大学;2015年
3 刘涛;基于硅微通道板的三维储能器件的研究[D];华东师范大学;2012年
相关硕士学位论文 前3条
1 常月琪;钛基自支撑电极在电化学储能器件中的研究[D];青岛科技大学;2016年
2 钟燕;基于氧化物的纳米储能器件复合电极的制备及其电化学性能研究[D];南京理工大学;2016年
3 童路攸;几种新型电极材料的制备及电化学储能[D];南京理工大学;2016年
，本文编号：2142702
本文链接：https://www.wllwen.com/kejilunwen/huagong/2142702.html