硝酸侵蚀环境喷射混凝土抗冻性试验研究

发布时间：2018-09-05 12:48

【摘要】：为研究硝酸侵蚀环境下喷射混凝土的抗冻性,对喷射混凝土和钢纤维喷射混凝土进行硝酸溶液快速冻融试验,并与同配合比普通模筑混凝土对比,得出三者抗冻性的差异,通过分析混凝土含气量、混凝土孔隙平均弦长探究混凝土抗冻性差异的机理,结果表明:掺加钢纤维能有效改善喷射混凝土抗冻性能;喷射混凝土初始含气量高,孔径弦长小,这是造成其抗冻性优于普通模筑混凝土的原因。
[Abstract]:In order to study the frost resistance of shotcrete under nitric acid erosion environment, the rapid freeze-thaw test of shotcrete and steel fiber shotcrete was carried out in nitric acid solution, and compared with the common concrete with the same mixing ratio, the difference of frost resistance among the three was obtained. By analyzing the air content of concrete and the average chord length of concrete pore, the mechanism of frost resistance difference of concrete is explored. The results show that the addition of steel fiber can effectively improve the frost resistance of shotcrete, the initial air content of shotcrete is high, and the chord length of pore diameter is small. This is the reason that the frost resistance of concrete is better than that of ordinary concrete.
【作者单位】： 西安建筑科技大学土木工程学院;西部绿色建筑重点实验室协同创新中心;结构工程与抗震教育部重点实验室;
【基金】：国家自然科学基金(51278403) 教育部创新团队发展计划(IRT13089)
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 张兴元;;提高外墙釉面砖的抗冻性[J];陶瓷;1986年05期

2 冯方;;彩釉砖快速烧成工艺与抗冻性的关系[J];陶瓷;1990年05期

3 张士萍;董良峰;费正岳;;提高混凝土材料抗冻性措施的研究[J];混凝土;2011年10期

4 慕儒;缪昌文;田倩;李建平;孙伟;;氯化钠溶液环境中砼的抗冻性[J];水利水电施工;2001年04期

5 段献智;于德龙;丛亮;;混凝土气泡结构和抗冻性的关系初探[J];山西建筑;2012年17期

6 陈德玉;刘欢;唐凯靖;;再生骨料混凝土的抗冻性研究[J];施工技术;2011年11期

7 关耳;;苏联进行釉面瓷砖的抗冻性研究[J];陶瓷研究;1986年02期

8 鲍孝红;;提高混凝土土抗冻性和耐久性的方法[J];青海交通科技;2011年04期

9 文婧;朱卫中;朱广祥;;掺合料对膨胀混凝土强度和抗冻性的影响[J];低温建筑技术;2012年12期

10 付向红;;多步搅拌工艺对高性能混凝土强度和抗冻性的影响[J];混凝土;2014年02期

相关硕士学位论文 前4条

1 魏耀宇;高耐久性喷射混凝土的研究[D];哈尔滨工业大学;2017年

2 黄成洋;煤矸石取代粗集料的混凝土抗渗性和抗冻性研究[D];沈阳建筑大学;2015年

3 胡国强;中低强度混凝土抗冻性的试验研究[D];浙江工业大学;2011年

4 王宝卿;夯土建筑材料耐久性试验研究[D];西安建筑科技大学;2006年

，

本文编号：2224324