煅烧温度和模板剂含量对介孔氧化锆微球结构和性能的影响
发布时间：2018-10-18 10:19
【摘要】：以F127和十二烷基硫酸钠(SDS)为模板剂,采用溶胶凝胶法制备介孔氧化锆微球。研究了煅烧温度和模板剂含量对介孔微球结构和性能的影响。实验制得微球尺寸均一,直径900μm左右。研究发现样品的比表面积随煅烧温度的升高而减小,而平均孔径则随煅烧温度的升高呈变大趋势。低温煅烧后样品为纯的四方相氧化锆,600℃煅烧后的样品中开始出现单斜相。相同煅烧温度下,模板剂添加量多的样品比表面积和孔体积要大。模板剂添加量对样品的物相结构没有影响。
[Abstract]:Mesoporous zirconia microspheres were prepared by sol-gel method using F127 and sodium dodecyl sulfate (SDS) as templates. The effects of calcination temperature and template content on the structure and properties of mesoporous microspheres were studied. The microspheres are uniform in size and about 900 渭 m in diameter. It is found that the specific surface area decreases with the increase of calcination temperature, while the average pore size increases with the increase of calcination temperature. The samples calcined at low temperature were pure tetragonal zirconia, and monoclinic phase appeared in the samples calcined at 600 鈩，
本文编号：2278825
[Abstract]:Mesoporous zirconia microspheres were prepared by sol-gel method using F127 and sodium dodecyl sulfate (SDS) as templates. The effects of calcination temperature and template content on the structure and properties of mesoporous microspheres were studied. The microspheres are uniform in size and about 900 渭 m in diameter. It is found that the specific surface area decreases with the increase of calcination temperature, while the average pore size increases with the increase of calcination temperature. The samples calcined at low temperature were pure tetragonal zirconia, and monoclinic phase appeared in the samples calcined at 600 鈩，
本文编号：2278825
本文链接：https://www.wllwen.com/kejilunwen/huaxue/2278825.html
教材专著