聚晶金刚石的ELID精密磨削试验研究

发布时间：2018-01-02 14:43

本文关键词：聚晶金刚石的ELID精密磨削试验研究　出处：《制造技术与机床》2016年01期 　论文类型：期刊论文

【摘要】：针对聚晶金刚石刃口加工的精度低、效率低、刃磨质量差的问题,采用同步电解修锐(ELID)精密磨削技术,对聚晶金刚石进行了精密磨削试验研究。首先,通过单因素试验探究砂轮粒度、磨削角度、磨削深度、砂轮转速以及工件移动速度对加工刃口质量的影响;然后,利用正交试验获得各因素的优组合与优水平,确定了最优工艺参数;最后,以最优试验参数对聚晶金刚石刃口进行精密磨削加工,获得刃口崩缺平均值0.042μm的加工表面。研究表明:应用ELID精密磨削加工工艺,当采用与被磨金刚石粒度相当或略小粒度的铸铁结合剂金刚石砂轮,砂轮转速为1 400 r/min、45°磨削角、磨削深度为0.1μm、进给速度为2 m/min时,磨削效果最佳。
[Abstract]:For the processing of polycrystalline diamond blade of low precision, low efficiency, poor quality of grinding, using synchronous electrolytic dressing (ELID) grinding technology of polycrystalline diamond were studied by precision grinding. Firstly, by single factor test on grain size of grinding wheel, grinding angle, grinding depth, workpiece speed and grinding effect the moving speed of machining blade quality; then, the optimized combination of advantages and the level of each factor obtained by orthogonal test, the optimum process parameters; finally, precision grinding of polycrystalline diamond cutting edge to obtain optimal experimental parameters, edge chipping average processing surface of 0.042 m. The results show that: the application ELID precision grinding process and grinding, when the diamond size equal to or slightly smaller degree of cast iron bonded diamond grinding wheel, grinding wheel speed is 1400 r/min, 45 degree angle grinding, grinding depth is 0.1 M, feed When the speed is 2 m/min, the grinding effect is the best.

【作者单位】：北京工业大学机械工程与应用电子技术学院;山东省滨州学院机电工程系;
【基金】：国家自然科学基金委员会-中国工程物理研究院联合基金资助项目(10676001)
【分类号】：TG580.6;TQ163
【正文快照】： 聚晶金刚石具有高硬度、高耐磨性、高抗压强度、高导热性及小摩擦系数等优良特性,用其制作的刀具凭借极高的硬度和出色的耐磨性,迅速在汽车、航空和木材加工领域获得了广泛的应用,在切削技术的发展过程中起着重要的推动作用[1-2]。聚晶金刚石的优良性能也给它的加工带来了难度

【参考文献】