质子交换膜燃料电池用碳气凝胶载铂催化电极

发布时间：2018-01-27 08:52

本文关键词： 质子交换膜燃料电池碳气凝胶载体催化电极　出处：《南京工业大学学报(自然科学版)》2016年02期 　论文类型：期刊论文

【摘要】：采用乙二醇还原法,以碳气凝胶为载体制备碳气凝胶载铂催化电极(Pt/CA/CP),并制成燃料电池单电池。采用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X线衍射仪(XRD)对碳气凝胶载铂催化剂进行表征,铂颗粒均匀分散于碳气凝胶载体上,粒径集中为3~5 nm。采用循环伏安法(CV)对碳气凝胶载铂催化电极进行电化学性能评价,碳气凝胶载铂催化电极具有较高的催化剂利用率,采用燃料电池测试系统对单电池进行性能评价,碳气凝胶载铂催化电极单电池工作电压可大于0.9 V,电流密度接近1 A/cm~2。
[Abstract]:Carbon aerogel supported platinum catalyst electrode (Pt / CA / CPN) was prepared by ethylene glycol reduction method. A single fuel cell cell was prepared by scanning electron microscopy (SEM). The carbon aerogel supported platinum catalyst was characterized by transmission electron microscope (TEM) and X-ray diffractometer. The platinum particles were uniformly dispersed on the carbon aerogel carrier. The electrochemical performance of carbon aerogel supported platinum catalytic electrode was evaluated by cyclic voltammetry (CV). The results showed that carbon aerogel supported platinum catalyst electrode had high catalyst utilization. The performance of a single cell was evaluated by using a fuel cell test system. The operating voltage of a single cell with a carbon aerogel supported platinum catalytic electrode was greater than 0.9 V, and the current density was close to 1 A / cm ~ (2).
【作者单位】：山东省科学院新材料研究所山东省粘接材料重点实验室;山东物流集团清恒能源有限公司;南京工业大学材料科学与工程学院材料化学工程国家重点实验室;
【基金】：济南市青年科技明星计划(2013039) 材料化学工程国家重点实验室开放课题基金(KL13-13) 国家自然科学基金(51402176) 山东省优秀中青年科学家科研奖励基金(BS2013CL038) 山东省科技发展计划(2013YD02046) 山东省科学院青年基金(2013QN019)
【分类号】：TM911.4;O646
【正文快照】： (1.山东省科学院新材料研究所山东省粘接材料重点实验室,山东济南250014;2.山东物流集团清恒能源有限公司,山东济南250014;3.南京工业大学材料科学与工程学院材料化学工程国家重点实验室,江苏南京210009)质子交换膜燃料电池(PEMFC)以其转化效率高、能量密度和功率密度大、环境

【相似文献】