电石渣掺量对矿用充填胶固粉性能影响研究

发布时间：2018-01-29 01:38

本文关键词： 胶凝材料电石渣抗压强度水化产物　出处：《矿产综合利用》2017年01期 　论文类型：期刊论文

【摘要】：为了在矿用充填材料中更加合理的利用电石渣,本文在粉煤灰、水泥熟料、钢渣等掺量不变的情况下,研究电石渣掺量0%、0.5%、1%、1.5%、2%时对胶固粉浆体的凝结时间、抗压强度、流动性、微观结构、水化产物的影响。试验结果表明:在凝结时间方面,随着电石渣掺量的增加,凝结时间随之减少;在抗压强度方面,1%掺量的电石渣组相比较其他掺量组使胶凝材料的强度最高;能够生成更多的水化产物;通过SEM观测表明,胶凝材料的微观结构更加致密。
[Abstract]:In order to make more reasonable use of calcium carbide slag in mineral filling material, this paper studies the amount of calcium carbide slag of 0 ~ 0.5% and 1.5% under the condition that the amount of fly ash, cement clinker and steel slag is constant. (2) the effect of setting time, compressive strength, fluidity, microstructure and hydration product on the cement paste. The results show that the setting time increases with the increase of calcium carbide slag content. The setting time decreases; In terms of compressive strength, the strength of cementing material is the highest in 1% calcium carbide slag group compared with other groups. Can produce more hydration products; The results of SEM show that the microstructure of the cemented material is more compact.
【作者单位】：山东鲁泰物流有限公司;邹城市南屯煤矿学校;山东科技大学;
【基金】：国家自然科学基金煤炭联合基金重点项目(U1261205);国家自然科学基金资助(51304027) 山东省科技计划项目(2014GSF120012) 第56批中国博士后科学基金面上一等资助(2014M560567) 第八批中国博士后基金特别资助(2015T80730) 青岛市博士后研究人员应用研究项目资助
【分类号】：TQ177
【正文快照】： 电石渣是在乙炔气、聚氯乙烯、聚乙烯醇等工业产品的生产过程中,电石(Ca C2)水解后产生的工业废渣,电石渣的堆放不仅占用大量的土地,而且因电石渣易于流失扩散,会污染堆放场地附近的水资源、碱化土地,长时间堆放还可能因风干起灰,污染周边环境,电石渣属难以处理的工业废弃物之