不同状态再生细骨料对再生保温混凝土抗压强度的影响

发布时间：2018-01-29 11:03

  本文关键词： 再生细骨料 预湿 取代率 再生保温混凝土 抗压强度　出处：《科学技术与工程》2017年10期 　论文类型：期刊论文

【摘要】：研究了再生细骨料取代率及预湿状态对再生保温混凝土抗压强度的影响。研究结果表明:随着再生细骨料取代率的增加,再生保温混凝土的抗压强度先增后减;0%和50%预湿状态下,再生细骨料取代率为40%时,再生保温混凝土的抗压强度值最大;而100%预湿状态在取代率为20%时抗压强度最大。再生细骨料的预湿状态对混凝土的强度发展具有显著的影响,100%预湿状态下混凝土早期强度发展较快,但28 d抗压强度较小。
[Abstract]:Study on the recycled fine aggregate replace rate and pre wet state of recycled insulation concrete compressive strength. The results show that with the increase of replacement ratio of recycled fine aggregate, the compressive strength of recycled concrete insulation increase firstly and then decrease; 0% and 50% pre wet state, recycled fine aggregate replacement rate is 40%, the compressive strength of recycled the maximum thermal insulation concrete; and the 100% state in the pre wet replace rate is 20%. The maximum compressive strength of recycled fine aggregate pre wet strength development of the concrete state has significant influence on the early strength of concrete, 100% pre wet state of rapid development, but the 28 d compressive strength is small.

【作者单位】： 太原理工大学建筑与土木工程学院;
【基金】：国家自然科学基金(51508370,51678384)资助
【分类号】：TU528
【正文快照】： 基金(51508370,51678384)资助引用格式:赵敏,刘元珍,姜鲁,等.不同状态再生细骨料对再生保温混凝土抗压强度的影响[J].科学技术与工程,2017,17(10):281—285Zhao Min,Liu Yuanzhen,Jiang Lu,et al.Effect of the different states ofrecycled fine aggregate on the compressiv

【相似文献】

相关期刊论文 前7条

1 ;北京铭基建筑节能科技有限公司玻化微珠承重保温混凝土研制成功[J];粉煤灰综合利用;2014年03期

2 高莉;刘元珍;李珠;许丽;;冻融作用下玻化微珠保温混凝土的劈裂抗拉性能试验[J];中国科技论文;2014年05期

3 武潮;李珠;赵林;;玻化微珠保温混凝土耐久性研究[J];新型建筑材料;2013年02期

4 许家文;刘元珍;李珠;王文靖;;再生保温混凝土抗压和抗折试验研究[J];混凝土;2013年12期

5 张会芝;连跃宗;;再生保温混凝土的力学性能试验研究[J];新型建筑材料;2013年02期

6 胡达明;;自保温混凝土复合砌块热工性能检测方法研究[J];砖瓦;2014年02期

7 ;[J];;年期

，

本文编号：1473261