人行道用新型高强度高储水混凝土的研究

发布时间：2018-02-01 22:24

  本文关键词： 高储水混凝土 吸水率 强度 收缩率 抗冻性　出处：《新型建筑材料》2017年03期 　论文类型：期刊论文

【摘要】：以水泥、矿粉、粉煤灰、石灰、石膏为主要粉料,适当加入减水剂和纤维,用物理发泡法,制备高强度高储水混凝土。研究了在1000、1200、1300、1400 kg/m~3密度等级下,高强度高储水混凝土的浆体流动度、表观密度、强度、收缩率、吸水率、抗冻性之间的关系。结果表明,高强度高储水混凝土的抗压强度为14.2~33.0 MPa,48 h吸水率为16.2%~27.1%,抗冻性良好,可望成为一种海绵城市人行道用的材料。
[Abstract]:High strength and high water storage concrete was prepared with cement, mineral powder, fly ash, lime, gypsum as main powder, water reducing agent and fiber added properly, and high strength high water storage concrete was prepared by physical foaming method. The relationship between slurry fluidity, apparent density, strength, shrinkage, water absorption and frost resistance of high strength and high water storage concrete under the density grade of 1 300 ~ 1 400 kg/m~3. The compressive strength of high strength and high water storage concrete is 14.2g / 33.0 MPA / h and the water absorption rate is 16.2m27.1 / h, and the frost resistance is good. It is expected to be used as a material for spongy city sidewalks.
【作者单位】： 重庆大学材料科学与工程学院;重庆建工住宅建设有限公司;
【分类号】：TU528
【正文快照】： 0引言随着我国城镇化建设的迅速发展,城市规模急剧膨胀,城市绿化面积越来越少,取而代之的是大量的混凝土道路和地坪,这些材料吸热能力强,阻隔了土壤与地表的热量交换和湿度调度调节,产生了城市热岛效应[1]。为了减小城市热岛效应,各地都在大力推广透水混凝土路面。曾勇等[2]和

【相似文献】

相关期刊论文 前10条

1 冯方;;彩釉砖快速烧成工艺与抗冻性的关系[J];陶瓷;1990年05期

2 张士萍;董良峰;费正岳;;提高混凝土材料抗冻性措施的研究[J];混凝土;2011年10期

3 慕儒;缪昌文;田倩;李建平;孙伟;;氯化钠溶液环境中砼的抗冻性[J];水利水电施工;2001年04期

4 段献智;于德龙;丛亮;;混凝土气泡结构和抗冻性的关系初探[J];山西建筑;2012年17期

5 陈德玉;刘欢;唐凯靖;;再生骨料混凝土的抗冻性研究[J];施工技术;2011年11期

6 关耳;;苏联进行釉面瓷砖的抗冻性研究[J];陶瓷研究;1986年02期

7 鲍孝红;;提高混凝土土抗冻性和耐久性的方法[J];青海交通科技;2011年04期

8 文婧;朱卫中;朱广祥;;掺合料对膨胀混凝土强度和抗冻性的影响[J];低温建筑技术;2012年12期

9 付向红;;多步搅拌工艺对高性能混凝土强度和抗冻性的影响[J];混凝土;2014年02期

10 孙其斌;;如何提高混凝土的抗冻性[J];民营科技;2012年07期

相关会议论文 前1条

1 文婧;朱卫中;朱广祥;;聚丙烯纤维与掺合料对膨胀混凝土强度和抗冻性的影响[A];第八届全国混凝土耐久性学术交流会论文集[C];2012年

相关硕士学位论文 前3条

1 黄成洋;煤矸石取代粗集料的混凝土抗渗性和抗冻性研究[D];沈阳建筑大学;2015年

2 胡国强;中低强度混凝土抗冻性的试验研究[D];浙江工业大学;2011年

3 王宝卿;夯土建筑材料耐久性试验研究[D];西安建筑科技大学;2006年

，

本文编号：1483012