焙烧工艺对磁选提纯氧化铁的影响

发布时间：2018-02-04 02:25

本文关键词： 还原焙烧磁选废铁回收　出处：《上海大学学报(自然科学版)》2017年02期 　论文类型：期刊论文

【摘要】：以城市生活垃圾焚烧炉渣中的废铁表层氧化铁鳞为原料,通过粉碎-焙烧和磁选工艺提纯,制取工业合格的氧化铁原料,并研究了焙烧、磁场强度、粉末粒度等试验条件对磁选效果的影响.结果表明,在还原温度为750?C、还原时间为60 min、木炭质量配比为7%,磁场强度为0.10和0.08 T的条件下进行二次磁选,可以获得品位67.61%、铁回收率85.17%的氧化铁精粉.
[Abstract]:Iron oxide scale on the surface of waste iron from municipal solid waste incinerator slag was used as raw material to prepare industrial qualified iron oxide raw material by means of crushing roasting and magnetic separation process. The roasting and magnetic field intensity were studied. The effect of powder particle size and other experimental conditions on the magnetic separation efficiency is studied. The results show that the reduction temperature is 750? When the reduction time is 60 min, the charcoal mass ratio is 7, the magnetic field intensity is 0.10 and 0.08T, the grade of 67.61% can be obtained. Iron recovery of 85.17%% iron oxide powder.
【作者单位】：上海大学材料科学与工程学院;
【分类号】：TQ138.11
【正文快照】： 城市生活垃圾的处理方法主要有卫生填埋、高温堆肥和垃圾焚烧.随着焚烧设备和技术的发展,以及人们对生活垃圾处理“三化”(减量化、无害化、资源化)要求的提高,垃圾焚烧处理的比例快速增长.2011年我国垃圾焚烧的比例占15.9%,比2001年增长了12倍之多[1-6].城市垃圾焚烧后的炉渣

【相似文献】