窑烧石膏型精密铸造琉璃工艺品的常见铸造缺陷

发布时间：2018-02-11 02:24

  本文关键词： 窑烧 石膏型 精密铸造 琉璃工艺品 铸造缺陷　出处：《铸造技术》2017年09期 　论文类型：期刊论文

【摘要】：石膏型精密铸造工艺是琉璃工艺品的主要成形方法,其工序过程较多,容易出现铸造缺陷。采用窑烧石膏型精密铸造工艺进行琉璃工艺品铸造试验,采用体视显微镜等手段对琉璃铸造缺陷进行观察。试验结果表明,铸造琉璃工艺品的常见缺陷有气孔、残缺、裂纹、表面粗糙、砂眼、杂色等,这些缺陷的产生受到琉璃材料、铸型质量、铸造工艺等多方面的影响。要获得优质铸造琉璃工艺品,应从上述各方面进行全面控制。
[Abstract]:The gypsum mould precision casting technology is the main forming method of glass handicraft, its working procedure is more, and it is easy to appear casting defect. The casting experiment of glass handicraft is carried out by using kiln burning gypsum mould precision casting technology. The casting defects of cast glass were observed by stereoscopic microscope. The results show that the common defects of cast glass handicrafts are pores, defects, cracks, rough surfaces, sandholes, miscellaneous colors, etc. These defects are produced by glass materials. Casting quality, casting technology and other aspects of the impact. In order to obtain high-quality casting glaze handicrafts, should be from the above aspects of overall control.
【作者单位】： 广州番禺职业技术学院珠宝学院;广东省珠宝首饰工程技术研究中心;
【基金】：广东省珠宝首饰工程技术研究中心建设项目(粤科产学研字[2016]176号)
【分类号】：TQ174.6

【相似文献】

相关期刊论文 前6条

1 卓蓉晖,戴奇;石膏及混合料性能研究[J];中国建材科技;2005年03期

2 卓蓉晖;填料对石膏铸型混合料性能的影响[J];山东建材;2005年03期

3 牛俊坡;;石膏型卤水加热管结垢的原因分析及预防[J];盐业与化工;2014年06期

4 唐娜;张艳华;任成龙;蔡芳;王嘉宁;鞠兴文;;石膏型卤水体系硫酸钙结晶过程研究[J];盐业与化工;2011年01期

5 刘勇健，，庄虹;熔模石膏型混合材料性能及焙烧工艺的研究[J];广东有色金属学报;1994年02期

6 吴大天,袁泽普;首饰熔模铸造用石膏型材料的研究[J];化学世界;1989年09期

相关会议论文 前1条

1 王文忠;李美林;赵建华;;汽车轮胎铸造用模具石膏的工艺研究[A];2012中国建筑材料联合会石膏建材分会第三届年会暨第七届全国石膏技术交流大会及展览会论文集[C];2012年

相关硕士学位论文 前1条

1 康燕;石膏型混合料工艺性能研究[D];中北大学;2010年

本文编号：1501998