粉煤灰与煤矸石混凝土压剪强度试验研究与分析

发布时间：2018-02-23 18:01

  本文关键词： 粉煤灰 煤矸石 混凝土 抗压强度 抗剪强度 剪切角　出处：《煤矿安全》2017年09期 　论文类型：期刊论文

【摘要】：通过普通混凝土试样、10%粉煤灰混凝土试样、20%粉煤灰混凝土试样和煤矸石混凝土试样进行28 d抗压强度和抗剪强度试验。试验结果表明:10%粉煤灰混凝土试样、20%粉煤灰混凝土试样和煤矸石混凝土试样相比于普通混凝土试样28 d抗压强度分别下降了45.25%、55.89%、17.11%;4种混凝土试样抗剪强度与剪切角关系分别采用线性拟合和指数拟合,普通混凝土试样、10%粉煤灰混凝土试样和20%粉煤灰混凝土试样抗剪强度随剪切角衰减变化符合指数模型,煤矸石混凝土抗剪强度随剪切角衰减变化符合线性模型。
[Abstract]:The compressive strength and shear strength of 10% fly ash concrete sample and 20% coal gangue concrete sample were tested for 28 days. The test results showed that 20% pulverized coal was obtained from 10% fly ash concrete sample. Compared with ordinary concrete samples, the compressive strength of gray concrete samples and coal gangue concrete samples decreased by 45.25 in 28 days, and the shear strength and shear angle of four kinds of concrete samples were fitted by linear fitting and exponential fitting, respectively. The shear strength of 10% fly ash concrete sample and 20% fly ash concrete specimen of ordinary concrete accords with exponential model with shear angle attenuation, and the shear strength of coal gangue concrete with shear angle attenuation is linear model.
【作者单位】： 安徽理工大学土木建筑学院;
【基金】：国家安全监管总局安全生产重大事故防治关键技术科技资助项目(anhui-0003-2016AQ) 安徽省高校自然科学重大资助项目(KJ2015ZD20)
【分类号】：TU528

【相似文献】

相关期刊论文 前1条

1 王振威;;煤矸石混凝土的材料组成与配合比设计[J];科技与企业;2013年09期

相关硕士学位论文 前4条

1 李腾;煤矸石混凝土砌块基本性能的研究[D];内蒙古农业大学;2016年

2 李明泽;高性能煤矸石混凝土性能的研究[D];沈阳建筑大学;2014年

3 晏亮;煤矸石混凝土及其结构构件性能试验研究[D];天津大学;2013年

4 李英雄;微波辐照活化云南未燃煤矸石混凝土试验研究[D];昆明理工大学;2011年

，

本文编号：1527074