超细钢渣微粉的制备及其对脱硫石膏改性的研究

发布时间：2018-02-27 12:50

  本文关键词： 超细钢渣微粉 脱硫石膏 改性剂　出处：《新型建筑材料》2017年09期 　论文类型：期刊论文

【摘要】：通过预粉磨和终粉磨双系统高效去除钢渣中的金属铁,制备比表面积大于600 m~2/kg的超细钢渣微粉。然后将超细钢渣微粉作为改性剂,内掺入脱硫石膏中进行性能测试。结果表明,超细钢渣微粉可以有效改善脱硫石膏的性能,当超细钢渣微粉掺量为15%时,相较于未掺超细钢渣微粉的脱硫石膏,吸水率降低了5.8个百分点,7 d和28 d抗折强度分别下降了9.6%和9.0%;抗压强度分别提高了17.2%和23.9%。
[Abstract]:The ultrafine steel slag powder with specific surface area of more than 600mg / kg was prepared by removing metal iron from steel slag efficiently by the double system of pre-grinding and final grinding. Then the ultrafine steel slag powder was used as modifier and the performance was tested in desulphurized gypsum. The results showed that the specific surface area of the ultrafine steel slag powder was more than 600 mg / kg. Ultrafine steel slag powder can effectively improve the performance of desulphurization gypsum. When the content of ultrafine steel slag powder is 15, compared with the desulfurization gypsum without superfine steel slag powder, The water absorption decreased by 5.8 percentage points and the flexural strength at 7 and 28 days decreased by 9.6% and 9.0, respectively, and the compressive strength increased by 17.2% and 23.9respectively.
【作者单位】： 上海大学;上海宇培特种建材有限公司;上海海笠新型环保建材股份有限公司;
【分类号】：TQ177.37

【相似文献】

相关期刊论文 前7条

1 张晖;高卫波;张键;金强;;宝钢钢渣微粉及其胶凝材安定性和相容性研究[J];宝钢技术;2010年03期

2 李凯;伦云霞;李文武;;磨细钢渣微粉替代水泥的可行性研究[J];门窗;2013年05期

3 孙家瑛;张健;金强;张晖;;宝钢钢渣微粉用于水泥混凝土的安定性和与水泥、外加剂相容性试验研究[J];粉煤灰;2006年03期

4 陈晨;;钢渣微粉在混凝土中的应用研究[J];商品混凝土;2012年11期

5 顾金土;邢天鹏;郑方伟;;半终粉磨钢渣微粉生产线的设计和实践[J];水泥工程;2014年03期

6 巴明芳;柳俊哲;贺智敏;何俊;;钢渣微粉改性水泥基钢渣骨料混凝土的配制及性能[J];材料导报;2013年22期

7 石国平;;钢渣微粉加工工艺探讨[J];水泥技术;2010年05期

相关会议论文 前1条

1 陈砚生;靳志刚;;谈热焖法钢渣处理技术及钢渣微粉生产工艺的设计实践[A];东南十省市水泥发展论坛会刊[C];2007年

相关重要报纸文章 前1条

1 陈磊;我国首条钢渣微粉挤压联合粉磨生产线试产成功[N];中国建材报;2011年

相关硕士学位论文 前1条

1 柳东;日钢钢渣微粉在混凝土中的应用[D];济南大学;2014年

，

本文编号：1542746