新型外源性渗透修复材料对混凝土裂缝修复效果研究

发布时间：2018-02-28 00:46

本文关键词： 外源性修复材料混凝土裂缝修复微观结构　出处：《混凝土》2017年10期 　论文类型：期刊论文

【摘要】：采用扫描电镜等测试技术研究了新型外源性渗透修复材料性质、微观结构以及修复材料对混凝土裂缝的修复效果。研究结果表明:新型外源性渗透修复材料30 min后流动度为248 mm,28 d抗折和抗压强度分别达到11.4、62.6 MPa,抗拉黏结强度达到3.28MPa;其微观结构中含有C-S-H凝胶、AFt、CH等物质;表面缝宽约为1 mm的裂缝,采用修复材料修复后抗压强度恢复率为90.6%,修复材料的渗透深度为40 mm;缝宽为4 mm的裂缝,修复后抗压强度恢复率为121.4%。
[Abstract]:The properties of new exogenous osmotic repair materials were studied by scanning electron microscopy (SEM). The results show that the flowability of the new material is 248mm / 28d after 30 min, the flexural strength and compressive strength of the new material are 11.4 mm ~ 62.6 MPa, respectively, and the tensile bond strength is up to 11.4 mm ~ 62.6 MPa. The results show that the tensile bonding strength of the new material is 11.4 mm ~ (-1) mm ~ (-1) after 30 min. To 3.28 MPA, the microstructures of which contain C-S-H gel and AFT Ch, etc. The recovery rate of compressive strength is 90.6 and the depth of penetration is 40 mm for the crack with a width of about 1 mm, and 121.4 for the crack with a width of 4 mm.
【作者单位】：商丘工学院土木工程学院;天津城建大学材料科学与工程学院;华南理工大学亚热带建筑科学国家重点实验室;
【基金】：国家自然科学基金(51372163) 华南理工大学亚热带建筑科学国家重点实验室开放基金(2016ZB23)
【分类号】：TU528

【相似文献】