一种基于围压和应变率效应的动态本构模型在钢纤维混凝土中的应用

发布时间：2018-03-02 12:20

  本文选题：固体力学　切入点：钢纤维混凝土　出处：《兵工学报》2017年S1期 　论文类型：期刊论文

【摘要】：采用Φ75 mm大口径分离式霍普金森压杆装置对钢纤维体积率分别为0%、0.75%、1.50%的混凝土试件进行动态性能实验,得到了不同钢纤维含量及不同应变率下材料的应力-应变全曲线。实验结果表明,钢纤维的加入增强了混凝土的韧性,并且随着纤维含量及应变率的增加,钢纤维混凝土材料的峰值应变和峰值应力都随之提高。以此实验为基础提出了一种基于含围压和应变率效应的动态本构模型,并对实验曲线进行了拟合,取得了良好的拟合效果。结果表明所提本构模型是合理的,具有良好的应用价值。
[Abstract]:The dynamic properties of concrete specimens with volume ratio of 0.75% and 1.50% of steel fiber were tested by 桅 75mm split Hopkinson pressure bar device. The stress-strain curves of different steel fiber content and different strain rate are obtained. The experimental results show that the toughness of concrete is enhanced by the addition of steel fiber, and with the increase of fiber content and strain rate, The peak strain and peak stress of steel fiber reinforced concrete (SFRC) materials increase accordingly. A dynamic constitutive model based on the effect of confining pressure and strain rate is proposed, and the experimental curve is fitted. The results show that the proposed constitutive model is reasonable and has good application value.
【作者单位】： 南京理工大学瞬态物理国家重点实验室;
【基金】：国家自然科学基金项目(11402266、11672138、11472008) 瞬态物理国家重点实验室基金项目(61426040403162604005) 中央高校基本科研业务费专项资金项目(30916011348)
【分类号】：TU528.572

【相似文献】

相关期刊论文 前3条

1 项笑炎;张春晓;何翔;王武;张磊;;大变形时温度和应变率对沥青混凝土动态力学性能的影响[J];武汉理工大学学报;2012年11期

2 李敏;李宏男;张皓;王德斌;;中强混凝土应变率效应的试验研究与数值模拟[J];混凝土;2014年04期

3 熊益波;陈剑杰;胡永乐;王万鹏;;混凝土Johnson-Holmquist本构模型关键参数研究[J];工程力学;2012年01期

相关会议论文 前2条

1 项笑炎;张春晓;何翔;王武;张磊;;大变形时温度和应变率对沥青混凝土动态力学性能的影响[A];第3届全国工程安全与防护学术会议论文集[C];2012年

2 李磊;安二峰;杨军;;钢化玻璃应变率相关的动态本构关系[A];第七届中国功能材料及其应用学术会议论文集（第2分册）[C];2010年

相关博士学位论文 前1条

1 尚世明;普通混凝土多轴动态性能试验研究[D];大连理工大学;2013年

，

本文编号：1556500