静电纺丝聚砜支撑层制备正渗透复合膜

发布时间：2018-03-03 07:23

  本文选题：正渗透复合膜　切入点：静电纺丝　出处：《水处理技术》2017年08期 　论文类型：期刊论文

【摘要】：采用静电纺丝法制备了聚砜(PSf)纳米纤维作为正渗透复合膜的支撑层,在此基础上通过界面聚合反应制备了正渗透膜。考察了纺丝液自身性质,PSf含量以及溶剂N,N-二甲基甲酰胺(DMF)与N-甲基-2-吡咯烷酮(NMP)比例对PSf支撑层微观结构及其性能影响。结果表明,纺丝液的PSf质量分数为20%,NMP/DMF体积比为3/7时得到的纺丝纤维均匀无瑕疵,平均纤维直径为396 nm,平均孔径为1.34μm,孔隙率为75.77%。经界面聚合反应在PSf支撑层表面形成聚酰胺活性层,经测试其水通量为42.17 L/(m~2·h),比3种商品膜水通量提高了3倍以上。
[Abstract]:The polysulfone (PSF) nanofibers were prepared by electrospinning method as the support layer of the composite membrane. On the basis of this, the normal osmotic membrane was prepared by interfacial polymerization. The properties of spinning solution and the ratio of N- N- (dimethylformamide) to N- methyl-2-pyrrolidone (NMP) on the microstructure and properties of PSf supporting layer were investigated. The results show that, When the volume ratio of PSf / DMF is 3/7, the spinning fiber is uniform and flawless. The average fiber diameter is 396nm, the average pore diameter is 1.34 渭 m, and the porosity is 75.77.The polyamide active layer is formed on the surface of the PSf support layer by interfacial polymerization. The water flux is 42.17 L / m ~ (2) 路h ~ (-1), which is more than three times higher than that of three commercial membranes.
【作者单位】： 东华大学环境科学与工程学院国家环境保护纺织污染防治工程技术中心;
【分类号】：TQ051.893

【相似文献】

相关会议论文 前1条

1 陈登星;何涛;李雪梅;;正渗透泵膜支撑层的制备[A];第五届全国医药行业膜分离技术应用研讨会论文集[C];2012年

相关重要报纸文章 前1条

1 中科院自动化所RFID研究中心 刘禹;冷静面对应用热潮[N];计算机世界;2004年

相关博士学位论文 前1条

1 吕兴霖;聚酰胺正渗透复合膜污染及离子返混机理和调控技术研究[D];哈尔滨工业大学;2015年

相关硕士学位论文 前5条

1 李明明;基于筛网的薄层复合正渗透膜的制备及表征[D];中国海洋大学;2015年

2 陈国豪;新型FBAR及传感技术的研究[D];浙江大学;2016年

3 李亮;客户服务中心应用支撑层程序设计接口[D];西安电子科技大学;2002年

4 吴言;聚酰胺—聚砜复合正渗透膜制备条件对膜结构与膜性能的影响研究[D];北京林业大学;2015年

5 甘霏;烃类分子混合物沸石基膜分离过程模型化研究[D];北京化工大学;2008年

，

本文编号：1560071