镍石膏-钛矿渣复合胶凝材料的试验研究

发布时间：2018-03-03 18:08

  本文选题：镍石膏　切入点：生石灰　出处：《非金属矿》2017年04期 　论文类型：期刊论文

【摘要】：以未经改性的镍石膏、钛矿渣和P·O42.5水泥为主要原料制备镍石膏-钛矿渣复合胶凝材料,通过物理力学性能及微观性能测试,分别研究了生石灰、矿物掺合料、硫铝酸盐水泥掺量和养护制度对镍石膏-钛矿渣复合胶凝材料物理力学性能的影响。结果表明,以生石灰作为碱性激发剂,掺量在6%时效果最好;加入4%偏高岭土和2%硫铝酸盐水泥后,基体的凝结时间大大缩短,早期强度显著增加,后期强度也有所增长;养护制度对基体3d和7d强度影响较大,28 d强度保持一致。
[Abstract]:The nickel gypsum titanium slag composite cementitious material was prepared from unmodified nickel gypsum, titanium slag and P 路O 42.5 cement. The effect of sulphoaluminate cement content and curing system on the physical and mechanical properties of nickel-gypsum titanium slag composite cementing material. After the addition of 4% metakaolin and 2% sulphoaluminate cement, the setting time of the matrix was greatly shortened, the early strength was significantly increased, and the later strength was also increased, while the curing system had the same effect on the 3d and 7d strength of the matrix.
【作者单位】： 西南科技大学材料科学与工程学院;西南科技大学四川省非金属复合与功能材料重点实验室;
【基金】：西南科技大学横向项目(14zh0287);西南科技大学创新基金(16ycx022)
【分类号】：TQ177

【相似文献】

相关期刊论文 前10条

1 白永忠;佟田林;;用钛矿渣作矿化剂 提高熟料质量[J];建筑材料工业;1961年01期

2 方荣利,金成昌,许安益;钛矿渣的利用研究[J];矿产综合利用;1998年02期

3 张继东;高钛矿渣的粉磨特性研究[J];中国粉体技术;2005年01期

4 子浩,方方;开发利用废渣效益好[J];中国建材;1988年01期

5 潘宝风,谭克锋;新型钛矿渣砖的生产工艺研究[J];硫磷设计与粉体工程;2003年06期

6 李祖树;徐楚韶;;钛矿渣电硅热法冶炼硅钛铁合金的热力学研究[J];四川冶金;1993年04期

7 马建;;钛矿渣的利用[J];交通世界(运输.车辆);2013年04期

8 方荣利,金成昌,许安益;利用钛矿渣生产道路水泥的试验[J];水泥;1998年07期

9 赵凯;齐渊洪;郭培民;甄常亮;;含钛矿渣的生产及综合利用新进展[J];环境工程;2011年S1期

10 张继东;水淬高钛矿渣的粉磨性能研究[J];水泥工程;2004年04期

相关会议论文 前2条

1 杨合;赵娜;薛向欣;;碱—含钛矿渣水泥光催化性能的研究[A];中国硅酸盐学会2003年学术年会论文摘要集[C];2003年

2 杨合;赵娜;薛向欣;;碱—含钛矿渣水泥光催化性能的研究[A];中国硅酸盐学会2003年学术年会水泥基材料论文集（上册）[C];2003年

相关硕士学位论文 前3条

1 范志;钛矿渣—固硫灰辅助性胶凝材料的性能研究[D];西南科技大学;2015年

2 赵国华;高钛矿渣在高温熔融状态下的改性研究[D];西南科技大学;2015年

3 杨华美;高钛矿渣作为水工混凝土掺和料及骨料性能研究[D];长江科学院;2010年

，

本文编号：1562117