可用于无钢筋建造的超强超韧水泥基复合材料

发布时间：2018-03-05 00:36

  本文选题：超高延性水泥基复合材料(UHDCC)　切入点：断裂力学　出处：《同济大学学报(自然科学版)》2017年06期 　论文类型：期刊论文

【摘要】：基于断裂力学的设计理念,使用活性粉末,并以高强、高弹性模量的聚乙烯纤维作为增强材料,制备具有超高强度和超高延性的纤维水泥基复合材料(UHDCC).轴向拉伸试验、轴压试验、弹性模量试验和四点弯曲试验结果表明,UHDCC的极限拉应力强度可达20 MPa,对应的平均拉伸应变接近9%,轴向抗压强度超过110 MPa.四点弯曲试验结果表明,UHDCC的无筋整浇梁的弯曲性能达到配筋率1.5%的普通钢筋混凝土梁的水平,且具有良好的延性.
[Abstract]:Based on the design concept of fracture mechanics, using reactive powder and polyethylene fiber with high strength and high elastic modulus as reinforcements, UHDCC composites with ultra high strength and high ductility were prepared. Axial compression test, The results of elastic modulus test and four-point bending test show that the ultimate tensile stress intensity of UHDCC can reach 20 MPA, the corresponding average tensile strain is close to 9 and the axial compressive strength is more than 110 MPA. The bending behavior reaches the level of normal reinforced concrete beams with a reinforcement ratio of 1.5%. And it has good ductility.
【作者单位】： 同济大学结构工程与防灾研究所;
【基金】：国家自然科学基金(51478362) 上海市工程结构安全重点实验室开放课题(2016-KF08)
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 杜玉兵;荀勇;;织物增强水泥基复合材料研究与应用展望[J];材料导报;2007年01期

2 冯志远;;现代水泥基复合材料[J];内蒙古石油化工;2009年10期

3 冯修吉,杨德坡;高性能水泥基复合材料的研究与发展状况[J];新世纪水泥导报;1996年05期

4 王彩辉;孙伟;蒋金洋;孙国文;乔运峰;;水泥基复合材料在多尺度方面的研究进展[J];硅酸盐学报;2011年04期

5 邹君;;蔗渣纤维增强水泥基复合材料的研究及发展前景[J];广西轻工业;2011年11期

6 刘军;马欣;李瑶;;外掺料对秸秆水泥基复合材料性能的影响[J];辽宁工程技术大学学报(自然科学版);2010年02期

7 阚黎黎;施惠生;瞿广飞;宁平;;工程水泥基复合材料自愈合过程与产物[J];同济大学学报(自然科学版);2011年10期

8 陈兵,张东;新型水泥基复合材料的研究与应用[J];新型建筑材料;2000年04期

9 孙明清,李卓球,刘清平;水泥及水泥基复合材料的机敏性研究[J];材料导报;2002年05期

10 吴香国;韩相默;徐世p，

本文编号：1568038