硬化水泥净浆基于纳米压痕的相态识别与水化程度计算

发布时间：2018-03-10 06:46

  本文选题：硬化水泥净浆　切入点：纳米压痕　出处：《复合材料学报》2017年05期 　论文类型：期刊论文

【摘要】：采用纳米原位压痕手段测量硬化水泥净浆中单一相态的代表性微观力学性能,并采用纳米点阵压痕研究各相态的含量。研究对象囊括水灰比为0.3、0.4、0.5的纯水泥净浆和水灰比为0.3情况下含50%、70%矿渣掺量复合体系,共5种配比,以表征它们的相态分布和微观力学性质的异同点。掺矿渣的试件中含有明显多的复合相,因此提出三相模型测算复合相中未水化物的体积分数。此外,提出基于纳米压痕技术计算纯水泥和掺矿渣水泥试件水化程度的方法,结果吻合于热重分析的结果,其中纯水泥净浆中复合相较少,计算得到的水化程度优于对掺矿渣水泥试件的计算。
[Abstract]:The representative micromechanical properties of single phase in hardened cement paste were measured by nano-in-situ indentation. The content of each phase was studied by nano-lattice indentation. In order to characterize their phase distribution and micromechanical properties, there are many complex phases in the slag-doped samples. Therefore, a three-phase model is proposed to calculate the volume fraction of unhydrated compounds in the composite phase. A method for calculating the hydration degree of pure cement and slag cement based on nano-indentation technique is proposed. The results are in agreement with the results of thermogravimetric analysis, in which there are fewer composite phases in pure cement paste. The calculated hydration degree is better than that of the slag cement specimen.
【作者单位】： 清华大学土木工程系土木工程安全与耐久教育部重点实验室;
【基金】：国家自然科学基金(51578316)
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 李响;阎培渝;;高温养护对复合胶凝材料水化程度及微观形貌的影响[J];中南大学学报(自然科学版);2010年06期

2 王培铭;彭宇;刘贤萍;;聚合物改性水泥水化程度测定方法比较[J];硅酸盐学报;2013年08期

3 王欣;万朝均;胡伟伟;;水泥石的干燥收缩及其与水化程度的关系[J];中国建材科技;2011年04期

4 李响;阿茹罕;阎培渝;;水泥-粉煤灰复合胶凝材料水化程度的研究[J];建筑材料学报;2010年05期

5 勾密峰;管学茂;张海波;;水化程度对水泥基材料固化氯离子的影响[J];材料导报;2011年20期

6 郑建军;庞宪委;熊芳芳;;基于计算机模拟的水化程度预测方法[J];建筑材料学报;2008年04期

7 沈业青;宇海银;王秀华;宋波;孙红霞;刘守华;;石膏对阿利特-硫铝酸钡钙水泥水化程度及浆体组成的影响[J];安徽师范大学学报(自然科学版);2007年06期

8 陈昕;;复合水泥基材料中水泥的水化程度分析[J];科技信息;2012年31期

9 王志亮;丁庆军;黄修林;;两种表征粉煤灰-水泥复合浆体整体水化程度方法对比研究[J];武汉理工大学学报;2014年01期

10 石帅;邓敏;莫立武;;掺MgO超细水泥的膨胀性能及其水化程度[J];南京工业大学学报(自然科学版);2012年02期

，

本文编号：1592212