吉水高岭土原矿理化性能分析及成瓷应用的研究

发布时间：2018-03-10 19:28

  本文选题：吉水高岭土　切入点：理化性能　出处：《中国陶瓷》2017年11期 　论文类型：期刊论文

【摘要】：分析测试了吉水高岭土原矿和精矿的化学组成和矿物组成,并对吉水高岭土精矿的结构形貌、粒度分布和物理性能进行了研究。将吉水高岭土原矿替代龙岩高岭土应用于日用陶瓷泥料配方中,研究其加入量对泥料可塑性、干燥抗弯强度、干燥收缩和烧成收缩的影响。研究结果表明:吉水高岭土原矿的主要矿物组成为石英、白云母、高岭石和微斜长石,属高岭石类矿物,高岭石矿物呈片状不规则叠置排列;吉水高岭土精矿颗粒较粗,体积平均粒径为19.562μm,是一种中可塑性、粘结性一般的高岭土原料;在日用陶瓷配方泥料生产中,吉水高岭土原矿用量控制在30%~50%范围内,泥料工艺性能可满足生产要求。
[Abstract]:The chemical composition and mineral composition of the primary ore and concentrate of Jishui kaolin have been analyzed and tested, and the structure and morphology of the concentrate of Jishui kaolin have been studied. The particle size distribution and physical properties were studied. The jishui kaolin ore was used to replace Longyan kaolin in the formulation of daily ceramic clay, and the plasticity and dry bending strength of the clay were studied. The effects of drying shrinkage and sintering shrinkage. The results show that the main mineral composition of Jishui kaolinite is quartz, Muscovite, kaolinite and microplagioclase, which belong to kaolinite minerals, and kaolinite minerals are lamellar and irregular superposition. Jishui kaolin concentrate is a kind of kaolin raw material with medium plasticity and general adhesive property, with a coarse grain size of 19.562 渭 m in volume, and the raw ore amount of Jishui kaolinite is controlled within 30% in the production of daily ceramic formula. The technical properties of the slurry can meet the requirements of production.
【作者单位】： 中国轻工业陶瓷研究所;
【分类号】：TQ174.41

【相似文献】

相关期刊论文 前10条

1 张忠铭;张伯周;;柳家湾瓷石的理化性能及其特征[J];景德镇陶瓷;1974年01期

2 谭志诚,沈惠华,陈淑霞;乙二醇及其水溶液二元体系理化性能数据的测定[J];化学工程;1983年01期

3 侯明龙;对提高工业搪瓷瓷釉质量的探讨[J];玻璃与搪瓷;1990年04期

4 БерзоН;董来棋;;精选高岭土生产中新技术的利用途径[J];瓷器;1963年04期

5 郭宝琛,吴菊青;河北省徐水高岭土概况[J];江苏陶瓷;1989年04期

6 江锦明;郑国良;李国镇;;福建高岭土及其应用的研究[J];中国陶瓷;1990年01期

7 郑国良;;对景德镇东埠高岭土矿山调查报告[J];陶瓷简报;1962年02期

8 代长禄;Etsugo Kato;;高岭土矿物的红外研究[J];河北陶瓷;1978年03期

9 岳铭五;;高岭土的干燥方法[J];非金属矿;1979年04期

10 陈开惠;高岭土矿结晶构造特征和研究方法[J];中国陶瓷;1982年05期

，

本文编号：1594743